Nanostructural characterization and catalytic analysis of hybridized platinumphthalocyanine nanocomposites

Kenji Kaneko, Kazuki Furuya, Ana B. Hungria, Juan Carlos Hernandez-Garrido, Paul A. Midgley, Tsunenobu Onodera, Hitoshi Kasai, Yusuke Yaguchi, Hidetoshi Oikawa, Yohei Nomura, Hiroki Harada, Tatsumi Ishihara, Norio Baba

    研究成果: ジャーナルへの寄稿学術誌査読

    6 被引用数 (Scopus)

    抄録

    Organic crystals, such as phthalocyanine nanocrystal, were successfully hybridized with Pt nanoparticles using a nanohybridization technique. The presence of highly dispersed Pt nanoparticles on the surface of phthalocyanine was confirmed by the combination of transmission electron microscopy and three-dimensional electron tomography. Catalytic activities of hybridized samples with different degrees of dispersions were also examined as oxygen reduction reactivity (ORR) with a linear potential sweep method. It was found that oxygen reduction activity increased with increasing Pt dispersion, and reasonably high ORR was observed on Pt-dispersed phthalocyanine nanocrystal even at 2 wt Pt loading.

    本文言語英語
    ページ(範囲)289-294
    ページ数6
    ジャーナルJournal of Electron Microscopy
    58
    5
    DOI
    出版ステータス出版済み - 10月 2009

    !!!All Science Journal Classification (ASJC) codes

    • 器械工学

    フィンガープリント

    「Nanostructural characterization and catalytic analysis of hybridized platinumphthalocyanine nanocomposites」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル