NaOH-Aided Platinum Nanoparticle Size Regulation on Polybenzimidazole-Wrapped Carbon Nanotubes for Use as Non-Humidified Polymer Electrolyte Fuel Cell Catalyst

Zehui Yang, Tsuyohiko Fujigaya, Naotoshi Nakashima

研究成果: Contribution to journalArticle査読

8 被引用数 (Scopus)

抄録

We describe a method to control the size of platinum nanoparticles (Pt-NPs) on poly[2,2′-(2,6-pyridine)-5,5′-bibenzimidazole] (PyPBI)-wrapped pristine multi-walled carbon nanotubes (MWNTs) without changing the loading amount by adding various concentrations of sodium hydroxide (NaOH) to the ethylene glycol aqueous solutions. The Pt-NP sizes decreased from 3.8±0.4 to 1.7±0.1 nm with increasing NaOH concentrations. The mass activity of the oxygen reduction reaction was 224 mA mgPt-1 for the electrocatalyst with 3 nm Pt-NPs, in which the power density reached 350 mW cm-2, which was 1.4 times higher than that of the electrocatalyst synthesized without NaOH (250 mW cm-2) at 120 °C and without any extra humidification. The electrocatalyst synthesized from a small amount of additional NaOH (0.5 mm) in the starting solution shows an enhanced performance and similar Pt stability. More importantly, the Pt-NP size showed no effect on the Pt stability owing to the use of the PyPBI.

本文言語英語
ページ(範囲)268-275
ページ数8
ジャーナルChemCatChem
8
1
DOI
出版ステータス出版済み - 1 7 2016

All Science Journal Classification (ASJC) codes

  • Catalysis
  • Physical and Theoretical Chemistry
  • Organic Chemistry
  • Inorganic Chemistry

フィンガープリント 「NaOH-Aided Platinum Nanoparticle Size Regulation on Polybenzimidazole-Wrapped Carbon Nanotubes for Use as Non-Humidified Polymer Electrolyte Fuel Cell Catalyst」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル