Narrow CoSi2 line formation on SiO2 by focused ion beam

A. Matsushita, Taizoh Sadoh, T. Tsurushima

研究成果: Chapter in Book/Report/Conference proceedingConference contribution

2 被引用数 (Scopus)

抄録

We propose a technique for formation of CoSi2 line structures on SiO2 films, which utilizes irradiation with 40 keV Si2+ FIB to the Co (14 nm)/Si (50 nm)/SiO2 (20 nm) stacked layer structures. Ion irradiation was performed at room temperature (RT) in order to prevent the thermal formation of cobalt silicide in regions without irradiation. After ion irradiation, unreacted Co layers remaining on the surfaces were removed by dipping the samples into the solution of HNO3:H2O2 = 1:3, and unreacted Si layers were removed by H3PO4 at 160 °C. The hot H3PO4 removes the deposited Si without etching the irradiated regions or SiO2 films. After the etching, the samples were heat treated at 700 and 900 °C for 20 min. As a result, cobalt silicide line structures were formed. The resistivity evaluated for samples heat treated at 700 and 900 °C was in agreement with that of CoSi and CoSi2, respectively. CoSi2 line structures with less than 200 nm width can be made by the procedure.

本文言語英語
ホスト出版物のタイトルProceedings of the International Conference on Ion Implantation Technology
出版社IEEE
ページ861-864
ページ数4
ISBN(印刷版)078034538X
出版ステータス出版済み - 12 1 1999
イベントProceedings of the 1998 International Conference on 'Ion Implantation Technology' Proceedings (IIT'98) - Kyoto, Jpn
継続期間: 6 22 19986 26 1998

出版物シリーズ

名前Proceedings of the International Conference on Ion Implantation Technology
2

その他

その他Proceedings of the 1998 International Conference on 'Ion Implantation Technology' Proceedings (IIT'98)
CityKyoto, Jpn
Period6/22/986/26/98

All Science Journal Classification (ASJC) codes

  • Engineering(all)

フィンガープリント 「Narrow CoSi<sub>2</sub> line formation on SiO<sub>2</sub> by focused ion beam」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル