Ni基超合金の長寿命域における中高温疲労特性

皮籠石 紀雄, 陳 強, 大坪 謙一, 燕 怒, 近藤 英二, 王 清遠

研究成果: ジャーナルへの寄稿学術誌査読

抄録

The fatigue properties of a nickel-base superalloy, Inconel 718, in long-life region up to 10<SUP>8</SUP> cycles were investigated under rotating bending at room temperature and elevated temperature of 300°C, 500°C and 600°C. S-N curves at 500°C and 600°C showed the stepwise shapes, though those in cases of room temperature and 300°C were the conventional one-step ones. All the fractures originated from the specimen surface at room temperature and 300°C, while the internal fractures occurred in long-life region beyond 10<SUP>7</SUP> cycles and the surface fractures at the stress levels over the horizontal line of S-N curves corresponding to the fatigue limit for the surface fracture at 500°C and 600°C. Intergranular crackings were observed at the origin of internal fracture.
寄稿の翻訳タイトルFatigue Properties of Ni-Base Superalloy in Long Life Region at Elevated Temperature
本文言語日本語
ページ(範囲)1192-1197
ページ数6
ジャーナルNihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
68
672
DOI
出版ステータス出版済み - 8月 25 2002

フィンガープリント

「Ni基超合金の長寿命域における中高温疲労特性」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル