Ni 基超合金の疲労き裂発生および初期伝ぱに及ぼす高温酸化膜の影響

皮籠石 紀雄, 大園 義久, 陳 強, 後藤 真宏, 田中 秀穂, 近藤 英二

研究成果: ジャーナルへの寄稿学術誌査読

抄録

Rotating bending fatigue tests were carried out for Ni base super alloy Inconel 718 at room temperature and elevated temperatures of 300°C, 500°C and 600°C in order to investigate the effect of surface oxidation at the elevated temperatures on the fatigue crack initiation and its early growth process. The fatigue strength was higher at the elevated temperatures than at room temperature when stress levels were low. This phenomenon was caused from that the growth of a crack smaller than the size of a few grains was suppresed at the elevated temperatures, though the growth of a larger crack was accelerated. The main reason for the suppression of the early growth of a small crack was a formation of oxide films on the specimen surface at the elevated temperatures.
寄稿の翻訳タイトルEffect of Oxide Films on a Fatigue Crack Initiation and its Early Growth of Ni-Base Super Alloy
本文言語日本語
ページ(範囲)839-844
ページ数6
ジャーナルNihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
64
620
DOI
出版ステータス出版済み - 4月 25 1998

フィンガープリント

「Ni 基超合金の疲労き裂発生および初期伝ぱに及ぼす高温酸化膜の影響」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル