Non-propagating crack at giga-cycle fretting fatigue limit

Yoshiyuki Kondo, Chu Sakae, Masanobu Kubota, Kazutoshi Yanagihara

研究成果: Contribution to journalArticle

5 引用 (Scopus)


We sometimes experience fretting fatigue fracture of industrial machines after a long period of operation. It has been a question whether the fatigue limit really exists in fretting fatigue or not. In this report, fretting fatigue tests in giga-cycle region up to 109 cycles were performed. There was a knee point in the S-N curve and it was verified that no fracture was observed up to 109 cycles. An electro-potential drop technique was developed to detect the micro-crack growth behavior of the fretting fatigue. It was shown that the micro-crack generated by fretting ceased to grow and became a non-propagating crack at fatigue limit. These results indicated that the fatigue limit can exist also in fretting fatigue. The infinite endurance limit can be achieved by the mechanism that initiated fretting fatigue cracks become non-propagating cracks.

ジャーナルNippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
出版物ステータス出版済み - 8 2004

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント Non-propagating crack at giga-cycle fretting fatigue limit' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用