OBSERVATION OF THE SECONDARY FAILURE NEAR THE TIP OF TRANSVERSE CRACKS IN A GFRP CROSS-PLY LAMINATE.

Hiroichi Ohira, Nobuhide Uda

研究成果: Chapter in Book/Report/Conference proceedingConference contribution

1 引用 (Scopus)

抜粋

Concerning the nonlinear behavior of a glass/epoxy cross-ply laminate under tension, experiment was performed to verify our previous predictions that some secondary failure will be produced near the tip of transverse cracks and the failure will prevail at relatively high load. Results were satisfactory. The secondary failure is a tree-shaped cracking. Based on the results, a new failure mechanism is proposed.

元の言語英語
ホスト出版物のタイトルUnknown Host Publication Title
出版者Technomic Publ Co
ページ515-522
ページ数8
ISBN(印刷物)0877625697
出版物ステータス出版済み - 1987

All Science Journal Classification (ASJC) codes

  • Engineering(all)

フィンガープリント OBSERVATION OF THE SECONDARY FAILURE NEAR THE TIP OF TRANSVERSE CRACKS IN A GFRP CROSS-PLY LAMINATE.' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用

    Ohira, H., & Uda, N. (1987). OBSERVATION OF THE SECONDARY FAILURE NEAR THE TIP OF TRANSVERSE CRACKS IN A GFRP CROSS-PLY LAMINATE.Unknown Host Publication Title (pp. 515-522). Technomic Publ Co.