Optical thin films grown by surface chemical reaction for high-power lasers

Zaitsu Shin-Ichi, Shinji Motokoshi, Takahisa Jitsuno, Masahiro Nakatsuka, Tatsuhiko Yamanaka

研究成果: ジャーナルへの寄稿Conference article

抜粋

We prepared optical thin films grown with surface chemical reactions using TiCl4 and H2O for TiO2. The nonuniformity of thickness distribution was under 1% over 240 mm in diameter. The structure TiO2 film grown at 25 °C was amorphous. The structure changed into polycrystalline with an increase of growth temperature up to 400 °C. Secondary ion mass spectrometry showed that chloride residents presented in the films at every growth temperature. However, these chloride residents could be removed by thermal annealing at 400 °C. The TiO2 film at the growth temperature of 25 °C had a laser-induced damage threshold of 5 J/cm2 for 1-ns, 1064 nm laser pulse. The damage threshold of TiO2 films decreased at higher growth temperature. Chloride in the films had no influence on the laser-induced damage threshold.

元の言語英語
ページ(範囲)546-552
ページ数7
ジャーナルProceedings of SPIE - The International Society for Optical Engineering
3889
出版物ステータス出版済み - 1 1 2000
外部発表Yes
イベントAdvanced High-Power Lasers - Osaka, Jpn
継続期間: 11 1 199911 5 1999

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Computer Science Applications
  • Applied Mathematics
  • Electrical and Electronic Engineering

フィンガープリント Optical thin films grown by surface chemical reaction for high-power lasers' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用