OS0523 析出強化型ステンレス鋼A286の疲労特性に及ぼす硬さの分布の影響(OS5-5 寿命予測,OS-5 材料の疲労挙動と損傷評価2)

呉 昊, 濱田 繋, 野口 博司

研究成果: Contribution to journalArticle

抄録

In order to clarify the relationship between fatigue strength and hardness of precipitation strengthening type stainless steel: A286, tensile tests, fatigue tests and Vickers hardness tests were performed. As a result of the tests, A286 steel have high tensile strength as well as low fatigue strength. Then, from the result of hardness test, there is large variability in hardness distribution of A286 steel. High hard zone and low hard zone were found in a specimen of A286 steel. The hardness of the zone in which many cracks initiated, is lower than the zone in which few cracks initiated. It is considered that high tensile strength is based on average both high hardness zone and low hardness zone when tensile test, and low fatigue strength was caused by the fatigue cracks which are easy to initiate and propagate in low hardness zone. Therefore, this is the reason why the fatigue strength ratio of A286 steel is lower than most steel.
寄稿の翻訳タイトルOS0523 The effects of distribution of hardness on fatigue property of precipitation strengthening stainless steel A286
本文言語日本語
ページ(範囲)_OS0523-1_-_OS0523-3_
ジャーナルM&M材料力学カンファレンス
2011
0
DOI
出版ステータス出版済み - 2011

フィンガープリント

「OS0523 析出強化型ステンレス鋼A286の疲労特性に及ぼす硬さの分布の影響(OS5-5 寿命予測,OS-5 材料の疲労挙動と損傷評価2)」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル