Oxidation-induced degradation of SOFC Ni anodes at high fuel utilizations

研究成果: 著書/レポートタイプへの貢献会議での発言

5 引用 (Scopus)

抄録

In the downstream of SOFC systems, higher oxygen partial pressure can cause oxidation-induced Ni anode degradation. In this study, we have investigated cell performance at high fuel utilizations for simulating situations around the system downstream. When the anode voltage was higher than a voltage threshold, the cell performance was stable. On the other hand, it became unstable associated with cell voltage oscillation when anode voltage was around or less than the threshold value. The threshold value was consistent with the anode potential derived from the oxygen partial pressure at the phase boundary at which both Ni and NiO coexist.

元の言語英語
ホスト出版物のタイトルSolid Oxide Fuel Cells 14, SOFC 2015
編集者K. Eguchi, S. C. Singhal
出版者Electrochemical Society Inc.
ページ1345-1352
ページ数8
エディション1
ISBN(電子版)9781607685395
DOI
出版物ステータス出版済み - 1 1 2015
イベント14th International Symposium on Solid Oxide Fuel Cells, SOFC 2015; held as part of the Electrochemical Society, ECS Conference on Electrochemical Energy Conversion and Storage - Glasgow, 英国
継続期間: 7 26 20157 31 2015

出版物シリーズ

名前ECS Transactions
番号1
68
ISSN(印刷物)1938-5862
ISSN(電子版)1938-6737

その他

その他14th International Symposium on Solid Oxide Fuel Cells, SOFC 2015; held as part of the Electrochemical Society, ECS Conference on Electrochemical Energy Conversion and Storage
英国
Glasgow
期間7/26/157/31/15

Fingerprint

Solid oxide fuel cells (SOFC)
Anodes
Degradation
Oxidation
Partial pressure
Electric potential
Oxygen
Phase boundaries
Threshold voltage

All Science Journal Classification (ASJC) codes

  • Engineering(all)

これを引用

Kawasaki, T., Sugimoto, J., Tachikawa, Y., Shiratori, Y., Taniguchi, S., & Sasaki, K. (2015). Oxidation-induced degradation of SOFC Ni anodes at high fuel utilizations. : K. Eguchi, & S. C. Singhal (版), Solid Oxide Fuel Cells 14, SOFC 2015 (1 版, pp. 1345-1352). (ECS Transactions; 巻数 68, 番号 1). Electrochemical Society Inc.. https://doi.org/10.1149/06801.1345ecst

Oxidation-induced degradation of SOFC Ni anodes at high fuel utilizations. / Kawasaki, T.; Sugimoto, J.; Tachikawa, Yuya; Shiratori, Yusuke; Taniguchi, Shunsuke; Sasaki, Kazunari.

Solid Oxide Fuel Cells 14, SOFC 2015. 版 / K. Eguchi; S. C. Singhal. 1. 編 Electrochemical Society Inc., 2015. p. 1345-1352 (ECS Transactions; 巻 68, 番号 1).

研究成果: 著書/レポートタイプへの貢献会議での発言

Kawasaki, T, Sugimoto, J, Tachikawa, Y, Shiratori, Y, Taniguchi, S & Sasaki, K 2015, Oxidation-induced degradation of SOFC Ni anodes at high fuel utilizations. : K Eguchi & SC Singhal (版), Solid Oxide Fuel Cells 14, SOFC 2015. 1 Edn, ECS Transactions, 番号 1, 巻. 68, Electrochemical Society Inc., pp. 1345-1352, 14th International Symposium on Solid Oxide Fuel Cells, SOFC 2015; held as part of the Electrochemical Society, ECS Conference on Electrochemical Energy Conversion and Storage, Glasgow, 英国, 7/26/15. https://doi.org/10.1149/06801.1345ecst
Kawasaki T, Sugimoto J, Tachikawa Y, Shiratori Y, Taniguchi S, Sasaki K. Oxidation-induced degradation of SOFC Ni anodes at high fuel utilizations. : Eguchi K, Singhal SC, 編集者, Solid Oxide Fuel Cells 14, SOFC 2015. 1 版 Electrochemical Society Inc. 2015. p. 1345-1352. (ECS Transactions; 1). https://doi.org/10.1149/06801.1345ecst
Kawasaki, T. ; Sugimoto, J. ; Tachikawa, Yuya ; Shiratori, Yusuke ; Taniguchi, Shunsuke ; Sasaki, Kazunari. / Oxidation-induced degradation of SOFC Ni anodes at high fuel utilizations. Solid Oxide Fuel Cells 14, SOFC 2015. 編集者 / K. Eguchi ; S. C. Singhal. 1. 版 Electrochemical Society Inc., 2015. pp. 1345-1352 (ECS Transactions; 1).
@inproceedings{8dcd73dcb89d4be19ef4d15a30a35c4b,
title = "Oxidation-induced degradation of SOFC Ni anodes at high fuel utilizations",
abstract = "In the downstream of SOFC systems, higher oxygen partial pressure can cause oxidation-induced Ni anode degradation. In this study, we have investigated cell performance at high fuel utilizations for simulating situations around the system downstream. When the anode voltage was higher than a voltage threshold, the cell performance was stable. On the other hand, it became unstable associated with cell voltage oscillation when anode voltage was around or less than the threshold value. The threshold value was consistent with the anode potential derived from the oxygen partial pressure at the phase boundary at which both Ni and NiO coexist.",
author = "T. Kawasaki and J. Sugimoto and Yuya Tachikawa and Yusuke Shiratori and Shunsuke Taniguchi and Kazunari Sasaki",
year = "2015",
month = "1",
day = "1",
doi = "10.1149/06801.1345ecst",
language = "English",
series = "ECS Transactions",
publisher = "Electrochemical Society Inc.",
number = "1",
pages = "1345--1352",
editor = "K. Eguchi and Singhal, {S. C.}",
booktitle = "Solid Oxide Fuel Cells 14, SOFC 2015",
edition = "1",

}

TY - GEN

T1 - Oxidation-induced degradation of SOFC Ni anodes at high fuel utilizations

AU - Kawasaki, T.

AU - Sugimoto, J.

AU - Tachikawa, Yuya

AU - Shiratori, Yusuke

AU - Taniguchi, Shunsuke

AU - Sasaki, Kazunari

PY - 2015/1/1

Y1 - 2015/1/1

N2 - In the downstream of SOFC systems, higher oxygen partial pressure can cause oxidation-induced Ni anode degradation. In this study, we have investigated cell performance at high fuel utilizations for simulating situations around the system downstream. When the anode voltage was higher than a voltage threshold, the cell performance was stable. On the other hand, it became unstable associated with cell voltage oscillation when anode voltage was around or less than the threshold value. The threshold value was consistent with the anode potential derived from the oxygen partial pressure at the phase boundary at which both Ni and NiO coexist.

AB - In the downstream of SOFC systems, higher oxygen partial pressure can cause oxidation-induced Ni anode degradation. In this study, we have investigated cell performance at high fuel utilizations for simulating situations around the system downstream. When the anode voltage was higher than a voltage threshold, the cell performance was stable. On the other hand, it became unstable associated with cell voltage oscillation when anode voltage was around or less than the threshold value. The threshold value was consistent with the anode potential derived from the oxygen partial pressure at the phase boundary at which both Ni and NiO coexist.

UR - http://www.scopus.com/inward/record.url?scp=84938802801&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84938802801&partnerID=8YFLogxK

U2 - 10.1149/06801.1345ecst

DO - 10.1149/06801.1345ecst

M3 - Conference contribution

AN - SCOPUS:84938802801

T3 - ECS Transactions

SP - 1345

EP - 1352

BT - Solid Oxide Fuel Cells 14, SOFC 2015

A2 - Eguchi, K.

A2 - Singhal, S. C.

PB - Electrochemical Society Inc.

ER -