Oxide anode derived from Sr-doped LaMnO 3 perovskite oxide for SOFCs using LaGaO 3 electrolyte

Tatsumi Ishihara, Satoko Fukui, Makiko Enoki, Hiroshige Matsumoto

研究成果: Contribution to journalArticle査読

18 被引用数 (Scopus)

抄録

Various oxides were investigated as a ceramic anode of solid oxide fuel cells (SOFCs) using LaGa O3 -based oxide electrolyte. It was found that the cell using Sr-doped LaMn O3 for anode exhibits a fairly large power density among the examined oxides for anode. Because the anodic overpotential as well as the electrical resistance decreased, the power density of the cell increased with increasing the amount of Sr doped for La site in LaMn O3, and the highest power density of the cell was obtained by using La0.5 Sr0.5 Mn O3 for anode. On this cell, the maximum power density was achieved to a value of 0.64 and 0.25 W cm2 at 1273 and 1073 K, respectively. After exposure of the cell to air at 1273 K for 24 h, almost the same power density was recovered by changing air to H2. X-ray diffraction measurement suggests that the perovskite phase of La0.5 Sr0.5 Mn O3 anode partially decomposed into La2 Mn O4, Mn O2, and SrMn O3 after the power generation measurement; however, small power density can only be achieved on the cell using Mn O2, SrMn O3, La2 Mn O4, and LaSrMn O4 for anode. Therefore, LaMn O3 perovskite phase doped with Sr is active as the anode of SOFCs, which is highly tolerant against oxidation.

本文言語英語
論文番号039611JES
ページ(範囲)A2085-A2090
ジャーナルJournal of the Electrochemical Society
153
11
DOI
出版ステータス出版済み - 2006

All Science Journal Classification (ASJC) codes

  • 電子材料、光学材料、および磁性材料
  • 再生可能エネルギー、持続可能性、環境
  • 表面、皮膜および薄膜
  • 電気化学
  • 材料化学

フィンガープリント

「Oxide anode derived from Sr-doped LaMnO <sub>3</sub> perovskite oxide for SOFCs using LaGaO <sub>3</sub> electrolyte」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル