Oxygen-annealing effects on superconducting properties of ErBa 2Cu3Oy, thin films fabricated by pulsed laser deposition method

Shigeru Horii, Masashi Mukaida, Yusuke Ichino, Kaname Matsumoto, Tohru Ohazama, Ataru Ichinose, Yutaka Yoshida, Atsushi Saito, Jun Ichi Shimoyama, Kohji Kishio

研究成果: Contribution to journalArticle査読

抄録

We report crystallographic and electrical properties of ErBa 2Cu3Oy/SrTiO3 (Er123/STO) films which were fabricated by the pulsed-laser-deposition (PLD) method in the temperature range of 720-780°C, and dramatic enhancement of critical current density (/c) by an oxygen post-annealing process. The PLD Er123/STO films were found to be crystallographically excellent in the deposition temperature region below 770°C from the intensity of diffraction peaks of 00l, the pole-figure of a reciprocal (102) plane and microstructures of the surface and the cross-section. Interestingly, in this temperature region, Jc values were clearly increased to the order of 1010 Am-2 by oxygen post-annealing in comparison with those of the as-grown films (0.3∼0.6 × 1010 Am-2). Enhancement of Jc was accomplished in a wide annealing temperature range of 350-500°C, which is corresponding with an annealing temperature range where the critical temperature shows over 90 K on a polycrystalline sample. On the other hand, Irreversibility fields were almost independent of the annealing temperature. These results indicated that insufficient carrier-doped region was partly existed even in a non-equilibrium process such as the PLD method. Therefore, homogenization of oxygen contents in a whole part of the Er123 film is crucially important for enhancement of critical current properties, which strongly suggests that the oxygen annealing is effective for improvement of functionality of devices in PLD-REBa2Cu3O, (RE: rare earth elements) thin films.

本文言語英語
ページ(範囲)748-755
ページ数8
ジャーナルNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
68
9
DOI
出版ステータス出版済み - 9 2004
外部発表はい

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「Oxygen-annealing effects on superconducting properties of ErBa <sub>2</sub>Cu<sub>3</sub>O<sub>y</sub>, thin films fabricated by pulsed laser deposition method」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル