Phase separation and lattice misfit in NiAl(β1)-Ni2AlTi(H)-NiTi(β2)system

K. Oh-ishi, Zenji Horita, Minoru Nemoto

    研究成果: Contribution to journalArticle査読

    25 被引用数 (Scopus)

    抄録

    The lattice misfits at interphase interfaces, NiAl(B2)-Ni2AlTi(L21) and Ni2AlTi(L21)-NiTi(B2), in a pseudobinary NiAl(B2)-NiTi(B2) system have been estimated by transmission electron microscopy. When the size of Ni2AlTi precipitates is smaller than a critical value, the precipitates keep their lattice coherency with the NiAl and NiTi matrices. After longer periods of aging the Ni2AlTi precipitates lose their coherency by introducing interface dislocations surrounding them. The coherency loss occurs catastrophically and the shape of the precipitates changes to a globular one after the loss of coherency, while keeping the cubic-cubic orientation relationship. Contrast experiments have revealed that the Burgers vectors of these misfit dislocations are of a〈100〉 type with the pure edge component lying nearby on the surface of the Ni2AlTi phase. The magnitudes of the lattice misfits at NiAl-Ni2AlTi and NiTi-Ni2AlTi interfaces have been estimated from the spacings of the misfit dislocations and found to increase with decreasing aging temperature in both the systems. The present results are compared with the previously reported theoretical and experimental values. A NiAl-NiTi pseudobinary phase diagram is proposed based upon microstructure observation, lattice misfit measurements and analytical electron microscopy.

    本文言語英語
    ページ(範囲)99-106
    ページ数8
    ジャーナルMaterials Transactions, JIM
    38
    2
    DOI
    出版ステータス出版済み - 2 1997

    All Science Journal Classification (ASJC) codes

    • 工学(全般)

    フィンガープリント

    「Phase separation and lattice misfit in NiAl(β<sub>1</sub>)-Ni<sub>2</sub>AlTi(H)-NiTi(β<sub>2</sub>)system」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル