Phase transformation and lattice-strain formation in Ti1.0v 1.1Mn0.9during first absorption and desorption

Saishun Yamazaki, Jin Nakamura, Kouji Sakaki, Yumiko Nakamura, Etsuo Akiba

研究成果: Contribution to journalArticle査読

3 被引用数 (Scopus)

抄録

We used powder X-ray diffraction (XRD) and Rietveld refinement to study phase transformation and the lattice strain introduced into each hydride phase of Ti1.0V1.1Mn0.9 during first absorption and desorption. Hydrogénation proceeded from a solid-solution phase to a dihydride phase via a monohydride phase. Each single-phase region was observed beside two clear plateau regions on the pressure-composition (P-C) isotherm. In contrast, the desorption P-C isotherm showed only one clear plateau, corresponding to a two-phase region of the dihydride and the monohydride. The plateau was connected to a two-phase region of the monohydride and a solid-solution phase, and to another region of solidsolution phases. The monohydride single-phase region was not clearly observed during desorption. Isotropic lattice strain was introduced, and increased with phase transformation during the first absorption. The strain increased further in the subsequent phase transformation during desorption, particularly upon formation of a solid-solution phase.

本文言語英語
ページ(範囲)586-590
ページ数5
ジャーナルMaterials Transactions
52
4
DOI
出版ステータス出版済み - 4 2011

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「Phase transformation and lattice-strain formation in Ti<sub>1.0</sub>v <sub>1.1</sub>Mn<sub>0.9</sub>during first absorption and desorption」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル