Pitting corrosion resistance of anodized aluminum alloy processed by severe plastic deformation

In Joon Son, Hiroaki Nakano, Satoshi Oue, Shigeo Kobayashi, Hisaaki Fukushima, Zenji Horita

    研究成果: Contribution to journalArticle査読

    9 被引用数 (Scopus)

    抄録

    The effect of equal-channel angular pressing (ECAP) on the pitting corrosion resistance of anodized Al and Al-Mg alloy was investigated by electrochemical techniques in a solution containing 0.25 mol/L of Alcl 3 and by surface analysis. The time required before initiating pitting corrosion of anodized Al was longer with ECAP than without, indicating improvement in the pitting corrosion resistance by application of ECAP. However, in anodized Al-Mg alloy, the pitting corrosion occurred earlier with ECAP than without, showing that the corrosion resistance was worse with ECAP than without. SEM and EPMA observation revealed that pitting corrosion of anodized Al occurred around the impurity precipitates and that the size of the impurity precipitate decreased as a result of the ECAP. The improvement in pitting corrosion resistance of anodized Al by ECAP appears to be attributable to a decrease in the size of impurity precipitates. On the other hand, in anodized Al-Mg alloy, cracks occurred in the anodic oxide films during initial corrosion and the cracks were larger with ECAP than without. It is assumed that the pitting corrosion was promoted by the cracks resulted from ECAP.

    本文言語英語
    ページ(範囲)534-540
    ページ数7
    ジャーナルNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
    70
    7
    DOI
    出版ステータス出版済み - 7 2006

    All Science Journal Classification (ASJC) codes

    • 凝縮系物理学
    • 材料力学
    • 金属および合金
    • 材料化学

    フィンガープリント

    「Pitting corrosion resistance of anodized aluminum alloy processed by severe plastic deformation」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル