Planar slip-driven fatigue crack initiation and propagation in an equiatomic CrMnFeCoNi high-entropy alloy

Kai Suzuki, Motomichi Koyama, Shigeru Hamada, Kaneaki Tsuzaki, Hiroshi Noguchi

研究成果: ジャーナルへの寄稿学術誌査読

26 被引用数 (Scopus)

抄録

High-cycle fatigue crack initiation and propagation in an equiatomic CrMnFeCoNi high-entropy alloy were investigated using smooth specimens. The microstructural deformation characteristics, i.e., planar dislocation slip, significantly affected the fatigue crack initiation and small fatigue crack propagation. The deformation localization associated with dislocation planarity led to multiple crack initiation on the slip planes. The crack propagation mechanism comprised crack formation on slip planes around the main crack tip and subsequent coalescence. The fatigue crack propagation mechanism shifted to Mode I type as the crack length increased.

本文言語英語
論文番号105418
ジャーナルInternational Journal of Fatigue
133
DOI
出版ステータス出版済み - 4月 2020

!!!All Science Journal Classification (ASJC) codes

  • モデリングとシミュレーション
  • 材料科学(全般)
  • 材料力学
  • 機械工学
  • 産業および生産工学

フィンガープリント

「Planar slip-driven fatigue crack initiation and propagation in an equiatomic CrMnFeCoNi high-entropy alloy」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル