Powder consolidation of Al-10wt% Fe alloy by High-Pressure Torsion

Jorge M. Cubero-Sesin, Zenji Horita

研究成果: Contribution to journalArticle

40 引用 (Scopus)


Mixtures of high-purity elemental powders of Al with an Fe content of 10. wt% were consolidated at room temperature by means of High-Pressure Torsion (HPT) and subsequently deformed to high levels of strain. Relative density of the consolidated disks was >99% even at low strains. The microstructure observation by transmission electron microscopy revealed that the alloy consisted of an ultrafine grained Al matrix with an average grain size of 145. nm. Supersaturation of Fe was estimated in the matrix to a maximum of ~1. wt% Fe by X-ray diffraction. The dispersion of secondary Fe-rich particles was quantified by scanning electron microscopy and image processing techniques. Hardness and tensile strength were improved significantly with straining by HPT, in direct correlation with grain refinement and potentiated by dissolution of Fe particles in the matrix. Excellent compromise of strength and ductility was achieved at intermediate levels of imposed strain.

ジャーナルMaterials Science and Engineering A
出版物ステータス出版済み - 12 15 2012

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント Powder consolidation of Al-10wt% Fe alloy by High-Pressure Torsion' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用