Preparation and dielectric property of (Li0.12Na 0.88)NbO3-based solid solutions

Nobuhiro Kumada, Naoko Ito, Akira Miura, Takahiro Takei, Satoshi Wada, Takayuki Watanabe

研究成果: ジャーナルへの寄稿記事

抜粋

Three solid solutions [(1-x)LNN-xBaTiO3 (BT), xBaZrO3 (BZ) and xK0.5Ba0.5Ti0.5Nb0.5O 3(KBTN)] based on (Li0.12Na0.88)NbO 3(LNN) with the rhombohedral symmetry were prepared by conventional solid state reaction and their dielectric property was investigated. In the LNN-BT system in x ≤ 0.6 a secondary phase was observed as well as the perovskite-type phase and the psudo-cubic and tetragonal single phases were observed in 0.7 ≤ x ≤ 0.94 and 0.95≤ x ̄ 1.0, respectively. In LNN-BZ and LNN-KBTN systems single phases of the compounds with the rhombohedral symmetry were formed in x ≤ 0.05. The length of the a-axis increased with content of BZ or KBTN and that of the c-axis was almost unchanged except x = 0.1 for LNN-BZ. The secondary phase with the tetragonal tungsten bronze-type (TTB) structure was observed in wide composition range of these solid solutions, and LixBa2NaNb5-xMxO15(M: Ti, Zr) with the TTB-type structure was prepared and their crystal structure and dielectric property were investigated.

元の言語英語
ページ(範囲)544-549
ページ数6
ジャーナルJournal of the Ceramic Society of Japan
121
発行部数1415
DOI
出版物ステータス出版済み - 7 2013
外部発表Yes

    フィンガープリント

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Chemistry(all)
  • Condensed Matter Physics
  • Materials Chemistry

これを引用