Preparation of Silicon Nitride Whiskers from Diatomaceous Earth: I, Reaction Conditions

Yukako Mizuhara, Masao Noguchi, Tatsumi Ishihara, Yusaku Takita

研究成果: ジャーナルへの寄稿記事

30 引用 (Scopus)

抄録

Whiskers and powder of silicon nitride were prepared by the carbothermal reduction and nitridation of diatomaceous earth in the presence of flowing N2 and NH3. The optimum temperature for the formation of Si3N4 whiskers was 1350°C and the yield reached almost 20% after 24 h. The α‐Si3N4 content decreased with increasing nitridation temperature. Yields of the whiskers were dependent on NH3 concentration and the total gas feed rate. The maximum yield of inside whiskers was obtained for a 25 vol% NH3/N2 mixture, while the maximum quantity of outside whiskers was produced for 75 vol% NH3/N2. The sum of the yield of the inside and outside whiskers increased with decreasing total gas feed rate. However, no nitridation of SiO2 was observed at a feed gas rate below 0.18 mmol·min−1. The yield of the inside whiskers increased gradually with increasing reaction time up to 36 h, whereupon a constant value was attained. Although the amount of outside whiskers produced was relatively small, the quantity seemed to increase until 60 h.

元の言語英語
ページ(範囲)109-113
ページ数5
ジャーナルJournal of the American Ceramic Society
78
発行部数1
DOI
出版物ステータス出版済み - 1 1 1995

Fingerprint

Diatomaceous Earth
Nitridation
Silicon nitride
Gases
Earth (planet)
Carbothermal reduction
Powders
Temperature
silicon nitride

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Materials Chemistry

これを引用

Preparation of Silicon Nitride Whiskers from Diatomaceous Earth : I, Reaction Conditions. / Mizuhara, Yukako; Noguchi, Masao; Ishihara, Tatsumi; Takita, Yusaku.

:: Journal of the American Ceramic Society, 巻 78, 番号 1, 01.01.1995, p. 109-113.

研究成果: ジャーナルへの寄稿記事

Mizuhara, Yukako ; Noguchi, Masao ; Ishihara, Tatsumi ; Takita, Yusaku. / Preparation of Silicon Nitride Whiskers from Diatomaceous Earth : I, Reaction Conditions. :: Journal of the American Ceramic Society. 1995 ; 巻 78, 番号 1. pp. 109-113.
@article{7fa42532254c4f7db1651c7a7a3778bd,
title = "Preparation of Silicon Nitride Whiskers from Diatomaceous Earth: I, Reaction Conditions",
abstract = "Whiskers and powder of silicon nitride were prepared by the carbothermal reduction and nitridation of diatomaceous earth in the presence of flowing N2 and NH3. The optimum temperature for the formation of Si3N4 whiskers was 1350°C and the yield reached almost 20{\%} after 24 h. The α‐Si3N4 content decreased with increasing nitridation temperature. Yields of the whiskers were dependent on NH3 concentration and the total gas feed rate. The maximum yield of inside whiskers was obtained for a 25 vol{\%} NH3/N2 mixture, while the maximum quantity of outside whiskers was produced for 75 vol{\%} NH3/N2. The sum of the yield of the inside and outside whiskers increased with decreasing total gas feed rate. However, no nitridation of SiO2 was observed at a feed gas rate below 0.18 mmol·min−1. The yield of the inside whiskers increased gradually with increasing reaction time up to 36 h, whereupon a constant value was attained. Although the amount of outside whiskers produced was relatively small, the quantity seemed to increase until 60 h.",
author = "Yukako Mizuhara and Masao Noguchi and Tatsumi Ishihara and Yusaku Takita",
year = "1995",
month = "1",
day = "1",
doi = "10.1111/j.1151-2916.1995.tb08368.x",
language = "English",
volume = "78",
pages = "109--113",
journal = "Journal of the American Ceramic Society",
issn = "0002-7820",
publisher = "Wiley-Blackwell",
number = "1",

}

TY - JOUR

T1 - Preparation of Silicon Nitride Whiskers from Diatomaceous Earth

T2 - I, Reaction Conditions

AU - Mizuhara, Yukako

AU - Noguchi, Masao

AU - Ishihara, Tatsumi

AU - Takita, Yusaku

PY - 1995/1/1

Y1 - 1995/1/1

N2 - Whiskers and powder of silicon nitride were prepared by the carbothermal reduction and nitridation of diatomaceous earth in the presence of flowing N2 and NH3. The optimum temperature for the formation of Si3N4 whiskers was 1350°C and the yield reached almost 20% after 24 h. The α‐Si3N4 content decreased with increasing nitridation temperature. Yields of the whiskers were dependent on NH3 concentration and the total gas feed rate. The maximum yield of inside whiskers was obtained for a 25 vol% NH3/N2 mixture, while the maximum quantity of outside whiskers was produced for 75 vol% NH3/N2. The sum of the yield of the inside and outside whiskers increased with decreasing total gas feed rate. However, no nitridation of SiO2 was observed at a feed gas rate below 0.18 mmol·min−1. The yield of the inside whiskers increased gradually with increasing reaction time up to 36 h, whereupon a constant value was attained. Although the amount of outside whiskers produced was relatively small, the quantity seemed to increase until 60 h.

AB - Whiskers and powder of silicon nitride were prepared by the carbothermal reduction and nitridation of diatomaceous earth in the presence of flowing N2 and NH3. The optimum temperature for the formation of Si3N4 whiskers was 1350°C and the yield reached almost 20% after 24 h. The α‐Si3N4 content decreased with increasing nitridation temperature. Yields of the whiskers were dependent on NH3 concentration and the total gas feed rate. The maximum yield of inside whiskers was obtained for a 25 vol% NH3/N2 mixture, while the maximum quantity of outside whiskers was produced for 75 vol% NH3/N2. The sum of the yield of the inside and outside whiskers increased with decreasing total gas feed rate. However, no nitridation of SiO2 was observed at a feed gas rate below 0.18 mmol·min−1. The yield of the inside whiskers increased gradually with increasing reaction time up to 36 h, whereupon a constant value was attained. Although the amount of outside whiskers produced was relatively small, the quantity seemed to increase until 60 h.

UR - http://www.scopus.com/inward/record.url?scp=0029172152&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0029172152&partnerID=8YFLogxK

U2 - 10.1111/j.1151-2916.1995.tb08368.x

DO - 10.1111/j.1151-2916.1995.tb08368.x

M3 - Article

AN - SCOPUS:0029172152

VL - 78

SP - 109

EP - 113

JO - Journal of the American Ceramic Society

JF - Journal of the American Ceramic Society

SN - 0002-7820

IS - 1

ER -