Pressure dependence of hydrogen-induced transformations in C15 Laves phase DyFe2 studied by pressure differential scanning calorimetry

Haiwen Li, Kazuhiro Ishikawa, kiyoshi aoki

研究成果: Contribution to journalArticle査読

抄録

By thermal analysis of DyFe2: (1) hydrogen absorption; (2) hydrogen-induced amorphization (HIA); (3) the precipitation of BiF3-type DyH3; and (4) the decomposition of the remaining amorphous hydride occur exothermically with increasing temperature at 1.0 MPa H2. Tp/Tm (the peak temperature/the melting temperature of DyFe2) for hydrogen absorption, HIA, the precipitation of DyH3 and the decomposition of the amorphous hydride are 0.28, 0.36, 0.43 and 0.48, respectively, which are closely related with kinetics of the transformations. The peak temperature Tp for HIA shows a large and negative pressure dependence, but that for the precipitation of DyH3 shows a small and positive one. As a consequence of such pressure dependence, HIA overlaps with the precipitation of DyH3 at 0.2 MPa H2, while the crystalline hydride decomposes directly into α-Fe and DyH3 at 0.1 MPa H2. The activation energy EA for hydrogen absorption, HIA, the precipitation of DyH3 and the decomposition of the amorphous hydride are calculated to be 56, 75, 308 and 162 kJ/mol Dy, respectively, which are closely related with the mechanism of HIA. The mechanism of HIA is discussed on the basis of the experimental results.
本文言語英語
ページ(範囲)49-58
ジャーナルJournal of Alloys and Compounds
388
DOI
出版ステータス出版済み - 2005

フィンガープリント

「Pressure dependence of hydrogen-induced transformations in C15 Laves phase DyFe2 studied by pressure differential scanning calorimetry」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル