Prestress loss and bending capacity of pre-cracked 40 year-old PC beams exposed to marine environment

Amry Dasar, Rita Irmawaty, Hidenori Hamada, Yasutaka Sagawa, Daisuke Yamamoto

研究成果: ジャーナルへの寄稿会議記事査読

8 被引用数 (Scopus)

抄録

Six prestressed concrete beams (PC beam) were used for evaluation, consist of four post-tension beams (PC-O) and two pre-tension beams (PC-R). In order to investigate the effect of crack on prestress loss and bending capacity after long-term exposed, prestressed concrete beams were pre-crack and then exposed to marine environment. Experimental work was carried out to evaluate PC beams performance after long-term exposed. In addition, visual observations and load bearing capacity test was carried out. Furthermore, evaluation of prestress loss conducted using three-point loading bending test and the remaining tendon forces in the beam were determined using Crack Re-opening Method. The experimental results revealed that prestress loss was increased due to corrosion of strand/wire which affected by the pre-crack on the prestressed beams. Approximately a prestress loss around 26% and 30% was recorded for post-tension and pre-tension beams respectively.

本文言語英語
論文番号02008
ジャーナルMATEC Web of Conferences
47
DOI
出版ステータス出版済み - 4月 1 2016
イベント3rd International Conference on Civil and Environmental Engineering for Sustainability, IConCEES 2015 - Melaka, マレーシア
継続期間: 12月 1 201512月 2 2015

!!!All Science Journal Classification (ASJC) codes

  • 化学 (全般)
  • 材料科学(全般)
  • 工学(全般)

フィンガープリント

「Prestress loss and bending capacity of pre-cracked 40 year-old PC beams exposed to marine environment」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル