Probing the differential methane decomposition behaviors of n-Ni/SiO2, n-Fe/SiO2 and n-Co/SiO2 catalysts prepared by co-precipitation cum modified Stöber method

U. P.M. Ashik, W. M.A. Wan Daud

研究成果: Contribution to journalArticle査読

15 被引用数 (Scopus)

抄録

n-Ni/SiO2, n-Fe/SiO2 and n-Co/SiO2 nano-catalysts were prepared by co-precipitation cum modified Stöber method and applied for thermocatalytic decomposition of methane in order to investigate their thermal stability and activity to produce greenhouse gas free hydrogen and nano-carbon. The mean particles sizes of the produced nano-catalysts obtained from BET analysis are 32.19 nm, 30.26 nm and 49.92 nm, respectively. Temperature programmed methane decomposition were conducted as a preliminary catalytic examination and further isothermal analyses were performed at 700 °C, 600 °C and 500 °C. Production of hydrogen at each experimental temperatures and corresponding carbon yield were measured. Among the three catalysts inspected, n-Ni/SiO2 was found to be the most efficient one for thermocatalytic methane decomposition. Furthermore, significant catalytic stability was observed with n-Ni/SiO2 at 500 °C and 600 °C. While, the rapid deactivation of the n-Fe/SiO2 and n-Co/SiO2 catalysts are attributed to particle agglomeration and the irregular formation of nano-carbon due to metal fragmentation. Physical and chemical characteristics of the produced nano-catalysts were investigated by N2 adsorption-desorption measurement (BET), X-ray diffraction (XRD), transmission electron microscopy (TEM) and hydrogen-temperature programmed reduction (H2-TPR). Produced nano-carbon were inspected with TEM, FESEM and XRD.

本文言語英語
ページ(範囲)67227-67241
ページ数15
ジャーナルRSC Advances
5
82
DOI
出版ステータス出版済み - 7 30 2015
外部発表はい

All Science Journal Classification (ASJC) codes

  • Chemistry(all)
  • Chemical Engineering(all)

フィンガープリント 「Probing the differential methane decomposition behaviors of n-Ni/SiO<sub>2</sub>, n-Fe/SiO<sub>2</sub> and n-Co/SiO<sub>2</sub> catalysts prepared by co-precipitation cum modified Stöber method」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル