Production and stability of radiation-induced defects in MgAl2O4 under electronic excitation

K. Yasuda, T. Yamamoto, S. Seki, K. Shiiyama, S. Matsumura

研究成果: Contribution to journalArticle査読

5 被引用数 (Scopus)

抄録

This paper investigates the formation process of radiation-induced defects in magnesium aluminate spinel and their stability using transmission electron microscopy, with emphasis on the effects of electronic excitation. Small interstitial-type dislocation loops disappeared under electron-induced electronic excitation. The elimination rate of the loops was found to be one order higher than for α-alumina. The disappearance of dislocation loops by a dissociation mechanism into isolated interstitials is discussed through analysis of the growth-and-shrink process of the loops. HARECXS analysis on cross section specimens irradiated with 350 MeV Au ions has shown the progress of cation disordering along ion tracks to be a function of electronic stopping power, (dE/dx)e. Cations were found to exchange their sites toward a random configuration. Such disordering appears from (dE/dx)e = 10 keV/nm, and increases in size with increasing (dE/dx)e to reach nearly 10 nm in diameter at 30 keV/nm, under an assumption of a fully disordered configuration.

本文言語英語
ページ(範囲)2834-2841
ページ数8
ジャーナルNuclear Instruments and Methods in Physics Research, Section B: Beam Interactions with Materials and Atoms
266
12-13
DOI
出版ステータス出版済み - 6 1 2008

All Science Journal Classification (ASJC) codes

  • Nuclear and High Energy Physics
  • Instrumentation

フィンガープリント 「Production and stability of radiation-induced defects in MgAl<sub>2</sub>O<sub>4</sub> under electronic excitation」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル