Pronounced effect of PbI2 nanoparticles doping on optoelectronic properties of PVA films for photo-electronic applications

Adel A. El-Zahhar, I. M. Ashraf, Abubakr M. Idris, Abdelrahman Zkria

研究成果: ジャーナルへの寄稿学術誌査読

2 被引用数 (Scopus)

抄録

Composite films of polyvinyl alcohol/lead iodide (PVA/PbI2) were prepared with different concentrations of PbI2 using low-cost casting process. The characteristics of the prepared films were analyzed by XRD and SEM. The XRD results showed increased crystalline nature with PbI2 content and the SEM micrographs revealed homogeneous particles distribution of PbI2 within the polymer. The optical parameters of PVA/PbI2 films were measured through UV–Vis absorption-transmittance spectroscopy. The indirect energy gap for PVA was found to be 4.75 eV, while the PVA/PbI2 film with 10 wt% PbI2 showed direct transition of 2.47 eV and indirect transition of 2.15 eV. The PVA film resistivity was found to be 1.79 × 109 Ω cm in the dark and decreased to1.85 × 108 Ω cm at 7000 lux. The film resistivity was found to decrease as the PbI2 content ratio increased up to 10 wt%. The results also showed gradual increase in photo sensitivity with increasing PbI2 content ratio in the composite films. The optical properties revealed that the composite films (PVA/PbI2) could be used in different optoelectronic applications.

本文言語英語
論文番号413604
ジャーナルPhysica B: Condensed Matter
630
DOI
出版ステータス出版済み - 4月 1 2022

!!!All Science Journal Classification (ASJC) codes

  • 電子材料、光学材料、および磁性材料
  • 凝縮系物理学
  • 電子工学および電気工学

フィンガープリント

「Pronounced effect of PbI2 nanoparticles doping on optoelectronic properties of PVA films for photo-electronic applications」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル