Proposed Strength Evaluation Method for Casting Material with Defects (Using Non-combustible Mg Alloy with Added-Si):(Using Non-combustible Mg Alloy with Added-Si)

Shigeru Hamada, Komei Hayashi, Toshiharu Matsumoto, Michiru Sakamoto, Hiroshi Noguchi

研究成果: Contribution to journalArticle査読

抄録

In order to evaluate a casting material which had a variable tensile strength, a strength evaluation method was proposed. Tensile tests were carried out on a specimen with a particular artificial defect as the fracture origin. The fracture origin size could be controlled using the proposed evaluation method. Therefore, the tensile test results, which had slight scatter, were obtained. However, the shape of the artificial defect was different from the casting defect, thus the effects of each defect on the tensile strength might be different. Both the critical stress intensity factors at the beginning of the unstable fracture were then compared, and it was clarified that the artificial defect and the casting defect had the same effect on the tensile strength. By this method, a non-combustible Mg alloy with added-Si, which contained large casting defects, could be evaluated. It was clarified that there was no difference of tensile strength between the noncombustible Mg alloys with 1% and 2% Si, and the relationship between the tensile strength and temperature was obtained.
本文言語英語
ページ(範囲)534-545
ページ数12
ジャーナルJournal of Solid Mechanics and Materials Engineering
5
10
DOI
出版ステータス出版済み - 2011

フィンガープリント 「Proposed Strength Evaluation Method for Casting Material with Defects (Using Non-combustible Mg Alloy with Added-Si):(Using Non-combustible Mg Alloy with Added-Si)」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル