Quantitative Evaluation of Heat Crack Initiation Condition Under Thermal Shock

Akio Sonoda, Suguru Kashiwagi, Shigeru Hamada, Hiroshi Noguchi

研究成果: Contribution to journalArticle査読


In this paper, we have proposed an evaluation method for the initiation conditions of heat crack under thermal shock using the tensile test of a notched specimen. In some materials, such as hot rolling rolls and dies for aluminum die-casting, there is a problem of heat crack initiation, and the evaluation of heat crack resistance using test pieces was difficult until now. The thermal stress and stress gradient that occurred in such material were analyzed by the finite element method (FEM). The maximum stress when tensile stress was applied to the material with a notch was compared to the stress gradient of the thermal stress. As a result, the quantitative evaluation during the initiation conditions of a heat crack for materials became possible.
ジャーナルJournal of Solid Mechanics and Materials Engineering
出版ステータス出版済み - 2008

フィンガープリント 「Quantitative Evaluation of Heat Crack Initiation Condition Under Thermal Shock」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。