疲労き裂伝ぱ寿命がばらつかなくなるき裂長さの定量的予測

相原 将敬, 濱田 繁, 野口 博司

研究成果: Contribution to journalArticle

抄録

<p>The fatigue crack growth behavior is not reproducible when a crack initiates and grows in a smooth material at a constant stress amplitude. However, a reproducible crack length <i>L</i><sub>0</sub> has been reported in which the variation in fatigue crack growth rate converges by observation of the crack growth behavior on the specimen surface. However, <i>L</i><sub>0</sub> volume has not been predicted quantitatively and the physical meaning of <i>L</i><sub>0</sub> is unknown, so it cannot be used in the design. Therefore, the authors analyzed the <i>L</i><sub>0</sub> quantitatively by analyzing the growth behavior of the three-dimensional crack front shape which grows inside the material. The aim is to develop a quantitative prediction method for <i>L</i><sub>0</sub> by analyzing the growth behavior by changing the crack front shape quantitatively. As a result, for the fatigue crack with the ideal crack shape, the possibility of the fatigue crack growth mechanism proposed by the authors was shown. For the complicated shape of the fatigue crack front shape, which depends on the hardness of the microstructures that randomly arranged in front of the fatigue crack, the difference of the stress intensity factor was explained by mechanics. It was shown that the possibility that <i>L</i><sub>0</sub> physically exists in the fatigue crack with the ideal crack front shape analyzed in this study.</p>
寄稿の翻訳タイトルQuantitative prediction of crack length where fatigue crack propagation life has no scatter
本文言語Japanese
ページ(範囲)OS0304
ジャーナルM&M材料力学カンファレンス
2019
0
DOI
出版ステータス出版済み - 2019

フィンガープリント 「疲労き裂伝ぱ寿命がばらつかなくなるき裂長さの定量的予測」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル