TEM observations and hydrogen thermal desorption analysis were performed to understand the relationship between microstructure and hydrogen absorption behavior in a V-bearing steel. The hydrogen absorption property was changed by controlling VC precipitation with changing tempering temperature from 573K to 973K. Hydrogen was absorbed into the specimen by cathode charging at a constant condition, and its content was examined by thermal desorption analysis. Energy-filtering and high-resolution TEM methods were employed to observe the size and distribution of VC precipitates. When the specimen was tempered at around 873K, the hydrogen absorption content was markedly increased; 4 times higher than that of the as-quenched specimen. TEM observations showed that this significant hydrogen absorption is attributed to nano-scale VC precipitates.
|ジャーナル||Journal De Physique. IV : JP|
|出版ステータス||出版済み - 10 2003|
|イベント||International Conference on Martensitic Transformations - Espoo, フィンランド|
継続期間: 6 10 2002 → 6 14 2002
All Science Journal Classification (ASJC) codes
- Physics and Astronomy(all)