Relaxation, Crystallization and Consolidation of Amorphous Alloy Powders

Akihisa Inoue, Tsuyoshi Masumoto, Tsuyoshi Yamamoto

研究成果: ジャーナルへの寄稿学術誌査読

2 被引用数 (Scopus)


The influence of applied pressure on the structural relaxation, glass transition, crystallization and consolidation for an amorphous phase was examined by using a typical glassy Pd48Ni32P20 alloy in a spherical powder or a ribbon form. The Pd-Ni-P alloy was chosen because of the existence of a wide supercooled liquid region in the temperature range below crystallization temperature (Tx). The relaxation and crystallization are significantly suppressed by the application of compressive load, presumably because of the increase in viscosity and the decrease in diffusivity. As a result, the pressing at a high temperature of 0.97TX is required to produce an amorphous bulk with high relative density. Furthermore, an intermediate annealing between pressings was found to be effective for the reduction of the enhanced viscosity. The multi-stage pressing treatment consisting of pressing and annealing enabled to produce a highly dense amorphous bulk even at a relatively low temperature near Tg.

ジャーナルJournal of the Japan Society of Powder and Powder Metallurgy
出版ステータス出版済み - 1991

!!!All Science Journal Classification (ASJC) codes

  • 機械工学
  • 産業および生産工学
  • 金属および合金
  • 材料化学


「Relaxation, Crystallization and Consolidation of Amorphous Alloy Powders」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。