Rheological analysis of surface relaxation process of monodisperse polystyrene films

Keiji Tanaka, Atsushi Takahara, Tisato Kajiyama

研究成果: ジャーナルへの寄稿記事

152 引用 (Scopus)

抄録

Surface glass transition temperature, Tgs, of monodisperse polystyrene (PS) films was determined from the temperature dependence of lateral force at a given scanning rate. The end groups of the PS were composed of sec-butyl group and a repeating unit terminated by proton. Tgs of the PS films was discerned to be markedly lower than its bulk Tg, Tgb, in the entire number-average molecular weight, Mn, range, 4.9 K to 1460 K. The Mn dependence of Tgs was analyzed on the basis of a simple power law. The exponent of Mn related to Tgs was -0.60±0.03 in contrast to the power of -0.5 from the Mayes scaling argument that is based on both chain ends being perfectly localized at the surface. This result implies that the surface localization of end groups of the PS used here is not complete. The Tgs extrapolated to the infinite Mn was found to be lower than the corresponding Tgb by approximately 20 K. The apparent activation energy of the surface αa-relaxation process for the PS obtained from Arrhenius plot was 230±10 kJ·mol-1, significantly smaller than that for the bulk PS. Also, it was shown on the basis of Ngai's coupling model that the cooperative motion at the surface can be achieved much easier than its internal bulk phase. Thus, the difference between the Tgs and the Tgb for the infinite Mn PS was explained in terms of the size and/or energy barrier reduction of the cooperative movement for the surface αa-relaxation process, which might be arisen from the existence of the free space presented to polymer segments at the surface.

元の言語英語
ページ(範囲)7588-7593
ページ数6
ジャーナルMacromolecules
33
発行部数20
DOI
出版物ステータス出版済み - 10 3 2000

Fingerprint

Surface relaxation
Polystyrenes
Relaxation processes
Arrhenius plots
Energy barriers
Protons
Polymers
Activation energy
Molecular weight
Scanning

All Science Journal Classification (ASJC) codes

  • Organic Chemistry
  • Polymers and Plastics
  • Inorganic Chemistry
  • Materials Chemistry

これを引用

Rheological analysis of surface relaxation process of monodisperse polystyrene films. / Tanaka, Keiji; Takahara, Atsushi; Kajiyama, Tisato.

:: Macromolecules, 巻 33, 番号 20, 03.10.2000, p. 7588-7593.

研究成果: ジャーナルへの寄稿記事

@article{484772ba7e9644dab5c35becfb5ab350,
title = "Rheological analysis of surface relaxation process of monodisperse polystyrene films",
abstract = "Surface glass transition temperature, Tgs, of monodisperse polystyrene (PS) films was determined from the temperature dependence of lateral force at a given scanning rate. The end groups of the PS were composed of sec-butyl group and a repeating unit terminated by proton. Tgs of the PS films was discerned to be markedly lower than its bulk Tg, Tgb, in the entire number-average molecular weight, Mn, range, 4.9 K to 1460 K. The Mn dependence of Tgs was analyzed on the basis of a simple power law. The exponent of Mn related to Tgs was -0.60±0.03 in contrast to the power of -0.5 from the Mayes scaling argument that is based on both chain ends being perfectly localized at the surface. This result implies that the surface localization of end groups of the PS used here is not complete. The Tgs extrapolated to the infinite Mn was found to be lower than the corresponding Tgb by approximately 20 K. The apparent activation energy of the surface αa-relaxation process for the PS obtained from Arrhenius plot was 230±10 kJ·mol-1, significantly smaller than that for the bulk PS. Also, it was shown on the basis of Ngai's coupling model that the cooperative motion at the surface can be achieved much easier than its internal bulk phase. Thus, the difference between the Tgs and the Tgb for the infinite Mn PS was explained in terms of the size and/or energy barrier reduction of the cooperative movement for the surface αa-relaxation process, which might be arisen from the existence of the free space presented to polymer segments at the surface.",
author = "Keiji Tanaka and Atsushi Takahara and Tisato Kajiyama",
year = "2000",
month = "10",
day = "3",
doi = "10.1021/ma000406w",
language = "English",
volume = "33",
pages = "7588--7593",
journal = "Macromolecules",
issn = "0024-9297",
publisher = "American Chemical Society",
number = "20",

}

TY - JOUR

T1 - Rheological analysis of surface relaxation process of monodisperse polystyrene films

AU - Tanaka, Keiji

AU - Takahara, Atsushi

AU - Kajiyama, Tisato

PY - 2000/10/3

Y1 - 2000/10/3

N2 - Surface glass transition temperature, Tgs, of monodisperse polystyrene (PS) films was determined from the temperature dependence of lateral force at a given scanning rate. The end groups of the PS were composed of sec-butyl group and a repeating unit terminated by proton. Tgs of the PS films was discerned to be markedly lower than its bulk Tg, Tgb, in the entire number-average molecular weight, Mn, range, 4.9 K to 1460 K. The Mn dependence of Tgs was analyzed on the basis of a simple power law. The exponent of Mn related to Tgs was -0.60±0.03 in contrast to the power of -0.5 from the Mayes scaling argument that is based on both chain ends being perfectly localized at the surface. This result implies that the surface localization of end groups of the PS used here is not complete. The Tgs extrapolated to the infinite Mn was found to be lower than the corresponding Tgb by approximately 20 K. The apparent activation energy of the surface αa-relaxation process for the PS obtained from Arrhenius plot was 230±10 kJ·mol-1, significantly smaller than that for the bulk PS. Also, it was shown on the basis of Ngai's coupling model that the cooperative motion at the surface can be achieved much easier than its internal bulk phase. Thus, the difference between the Tgs and the Tgb for the infinite Mn PS was explained in terms of the size and/or energy barrier reduction of the cooperative movement for the surface αa-relaxation process, which might be arisen from the existence of the free space presented to polymer segments at the surface.

AB - Surface glass transition temperature, Tgs, of monodisperse polystyrene (PS) films was determined from the temperature dependence of lateral force at a given scanning rate. The end groups of the PS were composed of sec-butyl group and a repeating unit terminated by proton. Tgs of the PS films was discerned to be markedly lower than its bulk Tg, Tgb, in the entire number-average molecular weight, Mn, range, 4.9 K to 1460 K. The Mn dependence of Tgs was analyzed on the basis of a simple power law. The exponent of Mn related to Tgs was -0.60±0.03 in contrast to the power of -0.5 from the Mayes scaling argument that is based on both chain ends being perfectly localized at the surface. This result implies that the surface localization of end groups of the PS used here is not complete. The Tgs extrapolated to the infinite Mn was found to be lower than the corresponding Tgb by approximately 20 K. The apparent activation energy of the surface αa-relaxation process for the PS obtained from Arrhenius plot was 230±10 kJ·mol-1, significantly smaller than that for the bulk PS. Also, it was shown on the basis of Ngai's coupling model that the cooperative motion at the surface can be achieved much easier than its internal bulk phase. Thus, the difference between the Tgs and the Tgb for the infinite Mn PS was explained in terms of the size and/or energy barrier reduction of the cooperative movement for the surface αa-relaxation process, which might be arisen from the existence of the free space presented to polymer segments at the surface.

UR - http://www.scopus.com/inward/record.url?scp=0034301508&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0034301508&partnerID=8YFLogxK

U2 - 10.1021/ma000406w

DO - 10.1021/ma000406w

M3 - Article

AN - SCOPUS:0034301508

VL - 33

SP - 7588

EP - 7593

JO - Macromolecules

JF - Macromolecules

SN - 0024-9297

IS - 20

ER -