Rotating bending fatigue property of SCM435 during electrochemical hydrogen charging

Ryo Kawakami, Kazumasa Kubota, Hisao Matsunaga

研究成果: Contribution to journalArticle査読


The method of rotating bending fatigue test under an electrochemical hydrogen-charging was established, by which the fatigue tests were carried out for a JIS-SCM435 to study the effect of hydrogen on fatigue strength. The fatigue life of the specimen was degraded by hydrogen -charging in relatively low fatigue life regime, where the slope of S-N curve for the hydrogen-charged specimens was equivalent to that for no-charged specimens. The fatigue strength on 50% failure probability at 107 cycles under the hydrogen-charging was slightly lower than that under the hydrogen-free condition. On the surface of the non-charged specimen that was run-out at 107 cycles, a number of cracks up to ≈100 μm in length was observed. By contrast, in the hydrogen-charged specimen, no crack was observed after the fatigue testing. These results suggested that the hydrogen-charging had a negative infiuence on the fatigue limit as well as fatigue life of the alloy used in this study.

ジャーナルNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
出版ステータス出版済み - 2020

All Science Journal Classification (ASJC) codes

  • 凝縮系物理学
  • 材料力学
  • 金属および合金
  • 材料化学


「Rotating bending fatigue property of SCM435 during electrochemical hydrogen charging」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。