Roughness-induced stress shielding effect in fatigue crack propagation under Mode II loading

Shigeru Hamada, Taro Suemasu, Shuto Fukudome, Motomichi Koyama, Masaharu Ueda, Hiroshi Noguchi

研究成果: Contribution to journalArticle

2 引用 (Scopus)

抜粋

Roughness-induced stress shielding effect under cyclic Mode II loading caused by fracture surface roughness, i.e., the effect of decreasing loading stress intensity factor K, is investigated. A fatigue crack propagation test by applying cyclic Mode II loading on a small textured material is performed. The decrease in K is a few percent quantitatively, and the decrease is sufficiently small to ignore. Using the failure surface observation results, we discuss the mechanism of the fatigue crack propagation during cyclic Mode II loading on the textured material and validate the repeated crack propagation mechanism of damage accumulation, void formation, and coalescence.

元の言語英語
ページ(範囲)245-256
ページ数12
ジャーナルInternational Journal of Fatigue
116
DOI
出版物ステータス出版済み - 11 2018

All Science Journal Classification (ASJC) codes

  • Modelling and Simulation
  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering
  • Industrial and Manufacturing Engineering

フィンガープリント Roughness-induced stress shielding effect in fatigue crack propagation under Mode II loading' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用