Selection of the massive-like δ-γ transformation due to nucleation of metastable δ phase in Fe-18 mass%Cr-Ni alloys with ni contents of 8, 11, 14 and 20 mass%

Tomohiro Nishimura, Ryota Matsubayashi, Kohei Morishita, Masato Yoshiya, Tomoya Nagira, Hideyuki Yasuda

研究成果: ジャーナルへの寄稿記事

3 引用 (Scopus)

抜粋

It has been realized that a massive-like transformation, in which δ phase (ferrite) transformed to γ phase (austenite) in the solid state during and after solidification, was selected in Fe-C steels. X-ray radiography confirmed that the massive-like transformation also occurred in Fe-18 mass%Cr-Ni alloys with Ni contents of 8, 11, 14 and 20 mass%Ni. According to the equilibrium phase diagram, δ phase is the primary phase in 8 and 11 mass%Ni alloys while γ phase in 14 and 20 mass%Ni alloys. Solidification was always initiated by nucleation of δ phase and consequently fine γ grains were formed by the massive-like transformation in 8 and 11 mass%Ni. On the other hand, nucleation of δ phase as a metastable phase was preferably selected at lower undercoolings (<50 K) in 14 and 20 mass%Ni and consequently the massive-like transformation occurred even in 14 and 20 mass%Ni alloys. Solidification of γ phase can be triggered by nucleation of δ phase followed by the massive-like transformation in the Fe-Cr-Ni with lower Cr/Ni values (the primary γ alloys). Moreover, the present study demonstrates that the massive-like transformation will be commonly observed in Fe-based alloys, in which δ and γ phases are competitive each other from a thermodynamic perspective.

元の言語英語
ページ(範囲)459-465
ページ数7
ジャーナルisij international
59
発行部数3
DOI
出版物ステータス出版済み - 3 2019

    フィンガープリント

All Science Journal Classification (ASJC) codes

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

これを引用