Self-supported LaGaO3-based honeycomb-type solid oxide fuel cell with high volumetric power density

Hao Zhong, Hiroshige Matsumoto, Tatsumi Ishihara, Akira Toriyama

研究成果: Contribution to journalArticle査読

13 被引用数 (Scopus)

抄録

A La0.9Sr0.1Ga0.8Mg0.2O3 (LSGM)-based honeycomb-type solid oxide fuel cell (SOFC) with a 0.5 mm thick electrolyte wall was successfully fabricated and operated. This cell shows a much higher volumetric power density than a ZrO2-based cell in the temperature range from 973 to 1173 K. Detailed results of internal resistance analysis suggest that IR loss is the predominant internal resistance of the cell. Furthermore, improved power density is achieved by decreasing LSGM electrolyte wall thickness. The effective area power densities are about 0.50 and 0.27 W/cm2 at 1073 and 973 K, respectively, using a 0.5 mm thick electrolyte wall. A 0.5 mm thick 4-wall cell was also successfully fabricated and operated at 1073 K; the estimated volumetric power density of this cell is as high as 600 W/L when five channels are used.

本文言語英語
ページ(範囲)1474-1477
ページ数4
ジャーナルSolid State Ionics
179
27-32
DOI
出版ステータス出版済み - 9 30 2008

All Science Journal Classification (ASJC) codes

  • 化学 (全般)
  • 材料科学(全般)
  • 凝縮系物理学

フィンガープリント

「Self-supported LaGaO<sub>3</sub>-based honeycomb-type solid oxide fuel cell with high volumetric power density」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル