Sharp cubic and octahedral morphologies of poly(vinylpyrrolidone)-stabilised platinum nanoparticles by polyol method in ethylene glycol: Their nucleation, growth and formation mechanisms

Nguyen Viet Long, Nguyen Duc Chien, Tomokatsu Hayakawa, Takashi Matsubara, Michitaka Ohtaki, Masayuki Nogami

    研究成果: ジャーナルへの寄稿記事

    11 引用 (Scopus)

    抄録

    Pt nanoparticles (NPs) were synthesised by a modified polyol method with the addition of silver nitrate. The results showed that the specific shapes of Pt NPs were influenced by the relevant factors, which are the contents of silver nitrate, synthetic time and temperature. A small content of silver nitrate has played an important role in determining their final shapes of platinum NPs. We observed that Pt NPs in the forms of very sharp shapes such as Pt cubes, octahedrons, cuboctahedrons and tetrahedrons have been obtained. In addition, the shape growth mechanisms and formation of Pt NPs have been studied. They exist in both cubic and octahedral shapes. Importantly, Pt nanocrystals can grow into main cubic and octahedral shapes for a short time less than 15 min. Moreover, Pt nanocrystals can also grow into different shapes from cubic and octahedral into spherical ones for several hours. Especially, they exhibited interesting shapes of multiple-branched Pt nanostructures because of their overgrowth and aggregations. Clearly, large cubic and octahedral Pt NPs of 160 nm diameter were observed. The growth and formation of large cubic and octahedral Pt NPs were due to the aggregation of Pt clusters or initial Pt seeds, even small Pt nanocrystals.

    元の言語英語
    ページ(範囲)133-149
    ページ数17
    ジャーナルJournal of Experimental Nanoscience
    7
    発行部数2
    DOI
    出版物ステータス出版済み - 3 1 2012

    Fingerprint

    Ethylene Glycol
    Polyols
    Ethylene glycol
    Platinum
    Nucleation
    Nanoparticles
    Silver Nitrate
    Nanocrystals
    Nitrates
    Silver
    Agglomeration
    polyol
    Seed
    Nanostructures

    All Science Journal Classification (ASJC) codes

    • Bioengineering
    • Biomedical Engineering
    • Materials Science(all)

    これを引用

    Sharp cubic and octahedral morphologies of poly(vinylpyrrolidone)-stabilised platinum nanoparticles by polyol method in ethylene glycol : Their nucleation, growth and formation mechanisms. / Long, Nguyen Viet; Chien, Nguyen Duc; Hayakawa, Tomokatsu; Matsubara, Takashi; Ohtaki, Michitaka; Nogami, Masayuki.

    :: Journal of Experimental Nanoscience, 巻 7, 番号 2, 01.03.2012, p. 133-149.

    研究成果: ジャーナルへの寄稿記事

    @article{c9f473eca630412f8fecd9299242f747,
    title = "Sharp cubic and octahedral morphologies of poly(vinylpyrrolidone)-stabilised platinum nanoparticles by polyol method in ethylene glycol: Their nucleation, growth and formation mechanisms",
    abstract = "Pt nanoparticles (NPs) were synthesised by a modified polyol method with the addition of silver nitrate. The results showed that the specific shapes of Pt NPs were influenced by the relevant factors, which are the contents of silver nitrate, synthetic time and temperature. A small content of silver nitrate has played an important role in determining their final shapes of platinum NPs. We observed that Pt NPs in the forms of very sharp shapes such as Pt cubes, octahedrons, cuboctahedrons and tetrahedrons have been obtained. In addition, the shape growth mechanisms and formation of Pt NPs have been studied. They exist in both cubic and octahedral shapes. Importantly, Pt nanocrystals can grow into main cubic and octahedral shapes for a short time less than 15 min. Moreover, Pt nanocrystals can also grow into different shapes from cubic and octahedral into spherical ones for several hours. Especially, they exhibited interesting shapes of multiple-branched Pt nanostructures because of their overgrowth and aggregations. Clearly, large cubic and octahedral Pt NPs of 160 nm diameter were observed. The growth and formation of large cubic and octahedral Pt NPs were due to the aggregation of Pt clusters or initial Pt seeds, even small Pt nanocrystals.",
    author = "Long, {Nguyen Viet} and Chien, {Nguyen Duc} and Tomokatsu Hayakawa and Takashi Matsubara and Michitaka Ohtaki and Masayuki Nogami",
    year = "2012",
    month = "3",
    day = "1",
    doi = "10.1080/17458080.2010.513017",
    language = "English",
    volume = "7",
    pages = "133--149",
    journal = "Journal of Experimental Nanoscience",
    issn = "1745-8080",
    publisher = "Taylor and Francis Ltd.",
    number = "2",

    }

    TY - JOUR

    T1 - Sharp cubic and octahedral morphologies of poly(vinylpyrrolidone)-stabilised platinum nanoparticles by polyol method in ethylene glycol

    T2 - Their nucleation, growth and formation mechanisms

    AU - Long, Nguyen Viet

    AU - Chien, Nguyen Duc

    AU - Hayakawa, Tomokatsu

    AU - Matsubara, Takashi

    AU - Ohtaki, Michitaka

    AU - Nogami, Masayuki

    PY - 2012/3/1

    Y1 - 2012/3/1

    N2 - Pt nanoparticles (NPs) were synthesised by a modified polyol method with the addition of silver nitrate. The results showed that the specific shapes of Pt NPs were influenced by the relevant factors, which are the contents of silver nitrate, synthetic time and temperature. A small content of silver nitrate has played an important role in determining their final shapes of platinum NPs. We observed that Pt NPs in the forms of very sharp shapes such as Pt cubes, octahedrons, cuboctahedrons and tetrahedrons have been obtained. In addition, the shape growth mechanisms and formation of Pt NPs have been studied. They exist in both cubic and octahedral shapes. Importantly, Pt nanocrystals can grow into main cubic and octahedral shapes for a short time less than 15 min. Moreover, Pt nanocrystals can also grow into different shapes from cubic and octahedral into spherical ones for several hours. Especially, they exhibited interesting shapes of multiple-branched Pt nanostructures because of their overgrowth and aggregations. Clearly, large cubic and octahedral Pt NPs of 160 nm diameter were observed. The growth and formation of large cubic and octahedral Pt NPs were due to the aggregation of Pt clusters or initial Pt seeds, even small Pt nanocrystals.

    AB - Pt nanoparticles (NPs) were synthesised by a modified polyol method with the addition of silver nitrate. The results showed that the specific shapes of Pt NPs were influenced by the relevant factors, which are the contents of silver nitrate, synthetic time and temperature. A small content of silver nitrate has played an important role in determining their final shapes of platinum NPs. We observed that Pt NPs in the forms of very sharp shapes such as Pt cubes, octahedrons, cuboctahedrons and tetrahedrons have been obtained. In addition, the shape growth mechanisms and formation of Pt NPs have been studied. They exist in both cubic and octahedral shapes. Importantly, Pt nanocrystals can grow into main cubic and octahedral shapes for a short time less than 15 min. Moreover, Pt nanocrystals can also grow into different shapes from cubic and octahedral into spherical ones for several hours. Especially, they exhibited interesting shapes of multiple-branched Pt nanostructures because of their overgrowth and aggregations. Clearly, large cubic and octahedral Pt NPs of 160 nm diameter were observed. The growth and formation of large cubic and octahedral Pt NPs were due to the aggregation of Pt clusters or initial Pt seeds, even small Pt nanocrystals.

    UR - http://www.scopus.com/inward/record.url?scp=84863891275&partnerID=8YFLogxK

    UR - http://www.scopus.com/inward/citedby.url?scp=84863891275&partnerID=8YFLogxK

    U2 - 10.1080/17458080.2010.513017

    DO - 10.1080/17458080.2010.513017

    M3 - Article

    AN - SCOPUS:84863891275

    VL - 7

    SP - 133

    EP - 149

    JO - Journal of Experimental Nanoscience

    JF - Journal of Experimental Nanoscience

    SN - 1745-8080

    IS - 2

    ER -