Shear mode growth and threshold of small fatigue cracks in SUJ2 bearing steel

Hisao Matsunaga, Satoshi Muramoto, Naoya Shomura, Masahiro Endo

研究成果: ジャーナルへの寄稿学術誌査読

14 被引用数 (Scopus)

抄録

The shear mode propagation and threshold behaviors of small, semi-elliptical fatigue cracks were investigated in the JIS-SUJ2 bearing steel. Fully-reversed torsional loading was combined with a static axial compressive load to obtain crack growth in the longitudinal direction of cylindrical specimens. Non-propagating cracks smaller than ≅1 mm in size were obtained (i) by decreasing the stress amplitude in tests using notched specimens, and (ii) by using smooth specimens in constant stress amplitude tests. The Mode II and Mode III threshold stress intensity factor ranges, δKIIth and δKIIIth, were estimated from the shapes and dimensions of non-propagating cracks. The threshold values decreased with a decrease in crack size, and there was no significant difference between δKIIth and δKIIIth- Wear on the crack faces was inferred by a powder and also by changes in microstructure in the wake of a crack. The Aftnth in the absence of interference of crack faces was estimated to be approximately 13MPa- m1/2 for a 1mm long crack.

本文言語英語
ページ(範囲)773-780
ページ数8
ジャーナルZairyo/Journal of the Society of Materials Science, Japan
58
9
DOI
出版ステータス出版済み - 9月 2009
外部発表はい

!!!All Science Journal Classification (ASJC) codes

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学

フィンガープリント

「Shear mode growth and threshold of small fatigue cracks in SUJ2 bearing steel」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル