Sintering nanocrystalline diopside from pulverized diopside crystals

Yumiko Tsubokawa, Masahiro Ishikawa

研究成果: Contribution to journalLetter査読

抄録

The sintering behavior of diopside nano-sized powder was studied. We successfully fabricated diopside nanosized powders from naturally occurring diopside single crystal (Ca0.92Na0.07Mn0.01Mg0.93Fe0.01Al0.06Si2O6). Di- opside polycrystalline is sintered from powders with an average particle size of <100 nm under argon flow at temperatures ranging from 1130-1280 °C for 0.5-20 h. The average grain size increased with increasing sintering time and sintering temperature while porosity remained nearly constant value of 3-4 vol%. The experimental data of grain growth at 1180 °C can be fit for the following equation G3 - G30 = kt, where G is the grain size after time t, G0 is the grain size at t = 0, and k is a rate constant.

本文言語英語
ページ(範囲)127-131
ページ数5
ジャーナルJournal of Mineralogical and Petrological Sciences
112
3
DOI
出版ステータス出版済み - 2017
外部発表はい

All Science Journal Classification (ASJC) codes

  • Geophysics
  • Geology

フィンガープリント 「Sintering nanocrystalline diopside from pulverized diopside crystals」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル