Size and distribution of micropores and voids in 5052 aluminum alloys during tensile deformation

Tomohiko Hojo, Mamoru Kikuchi, Kazuyuki Shimizu, Hiroyuki Toda, Akihisa Takeuchi, Eiji Akiyama

研究成果: Contribution to journalArticle

抜粋

Micropore growth and void initiation and growth behaviors of 5052 aluminum alloys during tensile deformation were observed by means of X-ray computed tomography (CT) using the X-ray image beamline (BL20XU) of the Japanese synchrotron radiation facility (SPring-8). Tensile tests were carried out in ambient and wet conditions. In 5052 alloy tensile tested in wet condition, the drop of stress followed by the maximum stress was remarkable, and the fracture strain was reduced in comparison with those of 5052 alloy tested in ambient condition. The number of fine micropores and voids decreased in 5052 alloy when plastic deformation started and the decrease in the amount of fine micropores and voids in the wet condition was less than those in ambient condition. These might be caused by the acceleration of micropore growth and void initiation and growth during tensile testing in wet condition.

元の言語英語
ページ(範囲)630-634
ページ数5
ジャーナルKeikinzoku/Journal of Japan Institute of Light Metals
68
発行部数11
DOI
出版物ステータス出版済み - 1 1 2018

All Science Journal Classification (ASJC) codes

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント Size and distribution of micropores and voids in 5052 aluminum alloys during tensile deformation' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用