Structure and codeposition behavior of Ni-W alloys electrodeposited from ammoniacal citrate solutions

Satoshi Oue, Hiroaki Nakano, Shigeo Kobayashi, Hisaaki Fukushima

研究成果: ジャーナルへの寄稿記事

26 引用 (Scopus)

抄録

The microstructure of Ni-W alloys electrodeposited at 1000 A m2 from ammoniacal citrate solutions was discussed in terms of their codeposition behavior. When the W content in the alloys was increased, the partial current efficiency of W first increased toward a maximum value and then decreased. This showed the existence of two characteristic alloy compositions, i.e., a W content at a maximum partial current efficiency of W and an upper limiting content of W. The deposition behavior of Ni-W alloys was explained by the multistep mechanism of the reduction of the electrochemically reduced W(IV) oxide to W by atomic hydrogen adsorbed using the unpaired 3d electrons of the freshly deposited Ni. X-ray diffraction (XRD) analysis revealed that alloys with a low W content consisted of a Ni solid solution, and the diffraction peaks became broader with an increase in W content. Ni-W alloys with high W contents showed a smooth surface composed of fine grains. Transmission electron microscopy studies revealed that the major phase in Ni-W alloys was the Ni solid solution, and the XRD pattern of the Ni-53.9 mass % W alloy revealed a halo pattern characteristic of an amorphous structure. This alloy consisted of crystal grains smaller than 10 nm in diameter.

元の言語英語
ジャーナルJournal of the Electrochemical Society
156
発行部数1
DOI
出版物ステータス出版済み - 1 1 2009

Fingerprint

Citric Acid
Solid solutions
Oxides
X ray diffraction analysis
Diffraction patterns
Hydrogen
Diffraction
Transmission electron microscopy
X ray diffraction
Crystals
Microstructure
Electrons
Chemical analysis

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Renewable Energy, Sustainability and the Environment
  • Surfaces, Coatings and Films
  • Electrochemistry
  • Materials Chemistry

これを引用

Structure and codeposition behavior of Ni-W alloys electrodeposited from ammoniacal citrate solutions. / Oue, Satoshi; Nakano, Hiroaki; Kobayashi, Shigeo; Fukushima, Hisaaki.

:: Journal of the Electrochemical Society, 巻 156, 番号 1, 01.01.2009.

研究成果: ジャーナルへの寄稿記事

@article{3d18fba588d2430d9621359c3b8bd85d,
title = "Structure and codeposition behavior of Ni-W alloys electrodeposited from ammoniacal citrate solutions",
abstract = "The microstructure of Ni-W alloys electrodeposited at 1000 A m2 from ammoniacal citrate solutions was discussed in terms of their codeposition behavior. When the W content in the alloys was increased, the partial current efficiency of W first increased toward a maximum value and then decreased. This showed the existence of two characteristic alloy compositions, i.e., a W content at a maximum partial current efficiency of W and an upper limiting content of W. The deposition behavior of Ni-W alloys was explained by the multistep mechanism of the reduction of the electrochemically reduced W(IV) oxide to W by atomic hydrogen adsorbed using the unpaired 3d electrons of the freshly deposited Ni. X-ray diffraction (XRD) analysis revealed that alloys with a low W content consisted of a Ni solid solution, and the diffraction peaks became broader with an increase in W content. Ni-W alloys with high W contents showed a smooth surface composed of fine grains. Transmission electron microscopy studies revealed that the major phase in Ni-W alloys was the Ni solid solution, and the XRD pattern of the Ni-53.9 mass {\%} W alloy revealed a halo pattern characteristic of an amorphous structure. This alloy consisted of crystal grains smaller than 10 nm in diameter.",
author = "Satoshi Oue and Hiroaki Nakano and Shigeo Kobayashi and Hisaaki Fukushima",
year = "2009",
month = "1",
day = "1",
doi = "10.1149/1.3006389",
language = "English",
volume = "156",
journal = "Journal of the Electrochemical Society",
issn = "0013-4651",
publisher = "Electrochemical Society, Inc.",
number = "1",

}

TY - JOUR

T1 - Structure and codeposition behavior of Ni-W alloys electrodeposited from ammoniacal citrate solutions

AU - Oue, Satoshi

AU - Nakano, Hiroaki

AU - Kobayashi, Shigeo

AU - Fukushima, Hisaaki

PY - 2009/1/1

Y1 - 2009/1/1

N2 - The microstructure of Ni-W alloys electrodeposited at 1000 A m2 from ammoniacal citrate solutions was discussed in terms of their codeposition behavior. When the W content in the alloys was increased, the partial current efficiency of W first increased toward a maximum value and then decreased. This showed the existence of two characteristic alloy compositions, i.e., a W content at a maximum partial current efficiency of W and an upper limiting content of W. The deposition behavior of Ni-W alloys was explained by the multistep mechanism of the reduction of the electrochemically reduced W(IV) oxide to W by atomic hydrogen adsorbed using the unpaired 3d electrons of the freshly deposited Ni. X-ray diffraction (XRD) analysis revealed that alloys with a low W content consisted of a Ni solid solution, and the diffraction peaks became broader with an increase in W content. Ni-W alloys with high W contents showed a smooth surface composed of fine grains. Transmission electron microscopy studies revealed that the major phase in Ni-W alloys was the Ni solid solution, and the XRD pattern of the Ni-53.9 mass % W alloy revealed a halo pattern characteristic of an amorphous structure. This alloy consisted of crystal grains smaller than 10 nm in diameter.

AB - The microstructure of Ni-W alloys electrodeposited at 1000 A m2 from ammoniacal citrate solutions was discussed in terms of their codeposition behavior. When the W content in the alloys was increased, the partial current efficiency of W first increased toward a maximum value and then decreased. This showed the existence of two characteristic alloy compositions, i.e., a W content at a maximum partial current efficiency of W and an upper limiting content of W. The deposition behavior of Ni-W alloys was explained by the multistep mechanism of the reduction of the electrochemically reduced W(IV) oxide to W by atomic hydrogen adsorbed using the unpaired 3d electrons of the freshly deposited Ni. X-ray diffraction (XRD) analysis revealed that alloys with a low W content consisted of a Ni solid solution, and the diffraction peaks became broader with an increase in W content. Ni-W alloys with high W contents showed a smooth surface composed of fine grains. Transmission electron microscopy studies revealed that the major phase in Ni-W alloys was the Ni solid solution, and the XRD pattern of the Ni-53.9 mass % W alloy revealed a halo pattern characteristic of an amorphous structure. This alloy consisted of crystal grains smaller than 10 nm in diameter.

UR - http://www.scopus.com/inward/record.url?scp=56749153997&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=56749153997&partnerID=8YFLogxK

U2 - 10.1149/1.3006389

DO - 10.1149/1.3006389

M3 - Article

VL - 156

JO - Journal of the Electrochemical Society

JF - Journal of the Electrochemical Society

SN - 0013-4651

IS - 1

ER -