Structure of a Gold(Ⅲ) Hydroxide and Determination of Its Solubility

Daisuke Kawamoto, Hiroaki Ando, Hironori Ohashi, Yasuhiro Kobayashi, Tetsuo Honma, Tamao Ishida, Makoto Tokunaga, Yoshihiro Okaue, Satoshi Utsunomiya, Takushi Yokoyama

研究成果: ジャーナルへの寄稿記事

抄録

<p>A representative gold(III) complex ion ([AuCl<sub>4</sub>]<sup>−</sup>), successively hydrolyzes to form [AuCl<sub>4−</sub><i><sub>n</sub></i>(OH)<i><sub>n</sub></i>]<sup>−</sup> (<i>n</i> = 0–4) in aqueous solution as the pH increases and, finally, precipitates. It has been referred to as "gold(III) hydroxide" for the past fifty years. However, whether the precipitate is gold(III) hydroxide (Au(OH)<sub>3</sub>) or hydrous gold(III) oxide (Au<sub>2</sub>O<sub>3</sub>·<i>n</i>H<sub>2</sub>O) has remained uncertain. Few studies have been conducted to determine its chemical and physical properties. The aim of this investigation is to identify the precipitate and to determine its solubility. The precipitate was X-ray amorphous. Based on the transmission electron microscopy (TEM) observation, the shape was spherical and the particle diameter was approximately 9 nm. From the results of <sup>197</sup>Au Mössbauer spectroscopy, Au L<sub>3</sub>-edge X-ray absorption (XA) spectroscopy and thermogravimetry/differential thermal analysis (TG/DTA) measurements, the precipitate composition was estimated to be Au(OH)<sub>3</sub>. Based on the composition, its structure was proposed to be a linear polymer. Moreover, its solubility at 298 K was determined to be 0.00120 g/100 g of H<sub>2</sub>O. This chemical and physical properties information of Au(OH)<sub>3</sub> is essential for gold chemistry, for example, for preparing supported gold catalyst.</p>
元の言語Japanese
ページ(範囲)1385-1390
ページ数6
ジャーナルBulletin of the Chemical Society of Japan
89
発行部数11
DOI
出版物ステータス出版済み - 2016

Fingerprint

Precipitates
Solubility
Gold
Chemical properties
Physical properties
X ray absorption spectroscopy
Chemical analysis
Differential thermal analysis
Oxides
Thermogravimetric analysis
Polymers
gold(III) hydroxide
Spectroscopy
Ions
Transmission electron microscopy
X rays
Catalysts

これを引用

Kawamoto, D., Ando, H., Ohashi, H., Kobayashi, Y., Honma, T., Ishida, T., ... Yokoyama, T. (2016). Structure of a Gold(Ⅲ) Hydroxide and Determination of Its Solubility. Bulletin of the Chemical Society of Japan, 89(11), 1385-1390. https://doi.org/10.1246/bcsj.20160228

Structure of a Gold(Ⅲ) Hydroxide and Determination of Its Solubility. / Kawamoto, Daisuke; Ando, Hiroaki; Ohashi, Hironori; Kobayashi, Yasuhiro; Honma, Tetsuo; Ishida, Tamao; Tokunaga, Makoto; Okaue, Yoshihiro; Utsunomiya, Satoshi; Yokoyama, Takushi.

:: Bulletin of the Chemical Society of Japan, 巻 89, 番号 11, 2016, p. 1385-1390.

研究成果: ジャーナルへの寄稿記事

Kawamoto, D, Ando, H, Ohashi, H, Kobayashi, Y, Honma, T, Ishida, T, Tokunaga, M, Okaue, Y, Utsunomiya, S & Yokoyama, T 2016, 'Structure of a Gold(Ⅲ) Hydroxide and Determination of Its Solubility', Bulletin of the Chemical Society of Japan, 巻. 89, 番号 11, pp. 1385-1390. https://doi.org/10.1246/bcsj.20160228
Kawamoto D, Ando H, Ohashi H, Kobayashi Y, Honma T, Ishida T その他. Structure of a Gold(Ⅲ) Hydroxide and Determination of Its Solubility. Bulletin of the Chemical Society of Japan. 2016;89(11):1385-1390. https://doi.org/10.1246/bcsj.20160228
Kawamoto, Daisuke ; Ando, Hiroaki ; Ohashi, Hironori ; Kobayashi, Yasuhiro ; Honma, Tetsuo ; Ishida, Tamao ; Tokunaga, Makoto ; Okaue, Yoshihiro ; Utsunomiya, Satoshi ; Yokoyama, Takushi. / Structure of a Gold(Ⅲ) Hydroxide and Determination of Its Solubility. :: Bulletin of the Chemical Society of Japan. 2016 ; 巻 89, 番号 11. pp. 1385-1390.
@article{f78bf2fea31b45cb9db845fb0b3ffe1d,
title = "Structure of a Gold(Ⅲ) Hydroxide and Determination of Its Solubility",
abstract = "A representative gold(III) complex ion ([AuCl4]−), successively hydrolyzes to form [AuCl4−n(OH)n]− (n = 0–4) in aqueous solution as the pH increases and, finally, precipitates. It has been referred to as {"}gold(III) hydroxide{"} for the past fifty years. However, whether the precipitate is gold(III) hydroxide (Au(OH)3) or hydrous gold(III) oxide (Au2O3·nH2O) has remained uncertain. Few studies have been conducted to determine its chemical and physical properties. The aim of this investigation is to identify the precipitate and to determine its solubility. The precipitate was X-ray amorphous. Based on the transmission electron microscopy (TEM) observation, the shape was spherical and the particle diameter was approximately 9 nm. From the results of 197Au M{\"o}ssbauer spectroscopy, Au L3-edge X-ray absorption (XA) spectroscopy and thermogravimetry/differential thermal analysis (TG/DTA) measurements, the precipitate composition was estimated to be Au(OH)3. Based on the composition, its structure was proposed to be a linear polymer. Moreover, its solubility at 298 K was determined to be 0.00120 g/100 g of H2O. This chemical and physical properties information of Au(OH)3 is essential for gold chemistry, for example, for preparing supported gold catalyst.",
author = "Daisuke Kawamoto and Hiroaki Ando and Hironori Ohashi and Yasuhiro Kobayashi and Tetsuo Honma and Tamao Ishida and Makoto Tokunaga and Yoshihiro Okaue and Satoshi Utsunomiya and Takushi Yokoyama",
year = "2016",
doi = "10.1246/bcsj.20160228",
language = "Japanese",
volume = "89",
pages = "1385--1390",
journal = "Bulletin of the Chemical Society of Japan",
issn = "0009-2673",
publisher = "The Chemical Society of Japan",
number = "11",

}

TY - JOUR

T1 - Structure of a Gold(Ⅲ) Hydroxide and Determination of Its Solubility

AU - Kawamoto, Daisuke

AU - Ando, Hiroaki

AU - Ohashi, Hironori

AU - Kobayashi, Yasuhiro

AU - Honma, Tetsuo

AU - Ishida, Tamao

AU - Tokunaga, Makoto

AU - Okaue, Yoshihiro

AU - Utsunomiya, Satoshi

AU - Yokoyama, Takushi

PY - 2016

Y1 - 2016

N2 - A representative gold(III) complex ion ([AuCl4]−), successively hydrolyzes to form [AuCl4−n(OH)n]− (n = 0–4) in aqueous solution as the pH increases and, finally, precipitates. It has been referred to as "gold(III) hydroxide" for the past fifty years. However, whether the precipitate is gold(III) hydroxide (Au(OH)3) or hydrous gold(III) oxide (Au2O3·nH2O) has remained uncertain. Few studies have been conducted to determine its chemical and physical properties. The aim of this investigation is to identify the precipitate and to determine its solubility. The precipitate was X-ray amorphous. Based on the transmission electron microscopy (TEM) observation, the shape was spherical and the particle diameter was approximately 9 nm. From the results of 197Au Mössbauer spectroscopy, Au L3-edge X-ray absorption (XA) spectroscopy and thermogravimetry/differential thermal analysis (TG/DTA) measurements, the precipitate composition was estimated to be Au(OH)3. Based on the composition, its structure was proposed to be a linear polymer. Moreover, its solubility at 298 K was determined to be 0.00120 g/100 g of H2O. This chemical and physical properties information of Au(OH)3 is essential for gold chemistry, for example, for preparing supported gold catalyst.

AB - A representative gold(III) complex ion ([AuCl4]−), successively hydrolyzes to form [AuCl4−n(OH)n]− (n = 0–4) in aqueous solution as the pH increases and, finally, precipitates. It has been referred to as "gold(III) hydroxide" for the past fifty years. However, whether the precipitate is gold(III) hydroxide (Au(OH)3) or hydrous gold(III) oxide (Au2O3·nH2O) has remained uncertain. Few studies have been conducted to determine its chemical and physical properties. The aim of this investigation is to identify the precipitate and to determine its solubility. The precipitate was X-ray amorphous. Based on the transmission electron microscopy (TEM) observation, the shape was spherical and the particle diameter was approximately 9 nm. From the results of 197Au Mössbauer spectroscopy, Au L3-edge X-ray absorption (XA) spectroscopy and thermogravimetry/differential thermal analysis (TG/DTA) measurements, the precipitate composition was estimated to be Au(OH)3. Based on the composition, its structure was proposed to be a linear polymer. Moreover, its solubility at 298 K was determined to be 0.00120 g/100 g of H2O. This chemical and physical properties information of Au(OH)3 is essential for gold chemistry, for example, for preparing supported gold catalyst.

U2 - 10.1246/bcsj.20160228

DO - 10.1246/bcsj.20160228

M3 - 記事

VL - 89

SP - 1385

EP - 1390

JO - Bulletin of the Chemical Society of Japan

JF - Bulletin of the Chemical Society of Japan

SN - 0009-2673

IS - 11

ER -