Study of factors in joint resistance for GdBCO coated conductors

T. Watanabe, T. Kamata, T. Maebatake, Ryo Teranishi, Takanobu Kiss, K. Yamada, Kenji Kaneko, M. Yoshizumi, T. Izumi

研究成果: ジャーナルへの寄稿Conference article

8 引用 (Scopus)

抄録

Joint techniques are important to manufacture long superconducting tapes. It has been reported that GdBa2Cu3Oy (GdBCO) coated conductors have higher critical current and critical temperature than YBCO. However, it was reported that the joint resistance of GdBCO was found higher than that of YBCO. In this paper, the elemental distribution maps were investigated to examine the cause of joint resistance. Electron microscopy analysis of GdBCO showed the reduction of oxygen in GdBCO layer. This oxygen reduction may cause degradation of superconducting properties and increase of Ag-GdBCO interfacial resistance, which may have led higher joint resistance in Ag/GdBCO.

元の言語英語
ページ(範囲)165-168
ページ数4
ジャーナルPhysics Procedia
45
DOI
出版物ステータス出版済み - 1 1 2013
イベント25th International Symposium on Superconductivity, ISS 2012 - Tokyo, 日本
継続期間: 12 3 201212 5 2012

Fingerprint

conductors
causes
oxygen
tapes
critical current
electron microscopy
critical temperature
degradation
temperature

All Science Journal Classification (ASJC) codes

  • Physics and Astronomy(all)

これを引用

Study of factors in joint resistance for GdBCO coated conductors. / Watanabe, T.; Kamata, T.; Maebatake, T.; Teranishi, Ryo; Kiss, Takanobu; Yamada, K.; Kaneko, Kenji; Yoshizumi, M.; Izumi, T.

:: Physics Procedia, 巻 45, 01.01.2013, p. 165-168.

研究成果: ジャーナルへの寄稿Conference article

Watanabe, T, Kamata, T, Maebatake, T, Teranishi, R, Kiss, T, Yamada, K, Kaneko, K, Yoshizumi, M & Izumi, T 2013, 'Study of factors in joint resistance for GdBCO coated conductors', Physics Procedia, 巻. 45, pp. 165-168. https://doi.org/10.1016/j.phpro.2013.04.078
Watanabe, T. ; Kamata, T. ; Maebatake, T. ; Teranishi, Ryo ; Kiss, Takanobu ; Yamada, K. ; Kaneko, Kenji ; Yoshizumi, M. ; Izumi, T. / Study of factors in joint resistance for GdBCO coated conductors. :: Physics Procedia. 2013 ; 巻 45. pp. 165-168.
@article{c81f0fcc5bd14410a73e320fab478a66,
title = "Study of factors in joint resistance for GdBCO coated conductors",
abstract = "Joint techniques are important to manufacture long superconducting tapes. It has been reported that GdBa2Cu3Oy (GdBCO) coated conductors have higher critical current and critical temperature than YBCO. However, it was reported that the joint resistance of GdBCO was found higher than that of YBCO. In this paper, the elemental distribution maps were investigated to examine the cause of joint resistance. Electron microscopy analysis of GdBCO showed the reduction of oxygen in GdBCO layer. This oxygen reduction may cause degradation of superconducting properties and increase of Ag-GdBCO interfacial resistance, which may have led higher joint resistance in Ag/GdBCO.",
author = "T. Watanabe and T. Kamata and T. Maebatake and Ryo Teranishi and Takanobu Kiss and K. Yamada and Kenji Kaneko and M. Yoshizumi and T. Izumi",
year = "2013",
month = "1",
day = "1",
doi = "10.1016/j.phpro.2013.04.078",
language = "English",
volume = "45",
pages = "165--168",
journal = "Physics Procedia",
issn = "1875-3892",
publisher = "Elsevier BV",

}

TY - JOUR

T1 - Study of factors in joint resistance for GdBCO coated conductors

AU - Watanabe, T.

AU - Kamata, T.

AU - Maebatake, T.

AU - Teranishi, Ryo

AU - Kiss, Takanobu

AU - Yamada, K.

AU - Kaneko, Kenji

AU - Yoshizumi, M.

AU - Izumi, T.

PY - 2013/1/1

Y1 - 2013/1/1

N2 - Joint techniques are important to manufacture long superconducting tapes. It has been reported that GdBa2Cu3Oy (GdBCO) coated conductors have higher critical current and critical temperature than YBCO. However, it was reported that the joint resistance of GdBCO was found higher than that of YBCO. In this paper, the elemental distribution maps were investigated to examine the cause of joint resistance. Electron microscopy analysis of GdBCO showed the reduction of oxygen in GdBCO layer. This oxygen reduction may cause degradation of superconducting properties and increase of Ag-GdBCO interfacial resistance, which may have led higher joint resistance in Ag/GdBCO.

AB - Joint techniques are important to manufacture long superconducting tapes. It has been reported that GdBa2Cu3Oy (GdBCO) coated conductors have higher critical current and critical temperature than YBCO. However, it was reported that the joint resistance of GdBCO was found higher than that of YBCO. In this paper, the elemental distribution maps were investigated to examine the cause of joint resistance. Electron microscopy analysis of GdBCO showed the reduction of oxygen in GdBCO layer. This oxygen reduction may cause degradation of superconducting properties and increase of Ag-GdBCO interfacial resistance, which may have led higher joint resistance in Ag/GdBCO.

UR - http://www.scopus.com/inward/record.url?scp=84902302985&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84902302985&partnerID=8YFLogxK

U2 - 10.1016/j.phpro.2013.04.078

DO - 10.1016/j.phpro.2013.04.078

M3 - Conference article

VL - 45

SP - 165

EP - 168

JO - Physics Procedia

JF - Physics Procedia

SN - 1875-3892

ER -