Study on atomization mechanism in spray coating of organic paint mixed with high-pressure carbon dioxide as a diluting solvent

Shin ichiro Kawasaki, Yuko Sakurai, Tatsuya Fujii

研究成果: Contribution to journalArticle査読

抄録

The atomization phenomenon in spray coating of organic paint mixed with high-pressure carbon dioxide as a diluting solvent was investigated. Industrial organic paint for automotive body coating was used without any diluting organic solvent. Under high-pressure conditions, CO2 was continuously mixed with the organic paint to reduce its viscosity to spray. The atomization phenomenon was investigated regarding the effects of high-pressure spraying and CO2 vaporization from droplets. The experimental conditions were varied such as the temperature, pressure, GtP (gas to paint ratio: CO2 gas flow rate [g/min]/paint flow rate [g/min]). The average droplet sizes under the CO2 spray at the 150 mm from nozzle (actual spray distance for automotive manufacturing) were measured by using a laser droplet size analyzer. The average droplet size was strongly affected by the fluid conditions (temperature and GtP), and the sizes were varied from 12 to 113 µm under conditions of 20–60 °C and 8–16 MPa. The minimum size of average droplet was 12 µm at 60 °C, 14 MPa, and 0.5 of GtP. The moderate heating (40–60 °C), high pressure (12–16 MPa) and two-phase (CO2-saturated paint and high pressure CO2) fluid spraying under high GtP condition in the nozzle are important factors to produce small and homogeneous droplet.

本文言語英語
論文番号105408
ジャーナルJournal of Supercritical Fluids
179
DOI
出版ステータス出版済み - 1 2022
外部発表はい

All Science Journal Classification (ASJC) codes

  • 化学工学(全般)
  • 凝縮系物理学
  • 物理化学および理論化学

フィンガープリント

「Study on atomization mechanism in spray coating of organic paint mixed with high-pressure carbon dioxide as a diluting solvent」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル