Study on factors in time-dependent dielectric breakdown degradation of Cu/low-k integration related to Cu chemical-mechanical polishing

Yohei Yamada, Nobuhiro Konishi, Junji Noguchi, Tomoko Jimbo, Syuhei Kurokawa, Toshiro Doi

研究成果: Contribution to journalArticle査読

6 被引用数 (Scopus)

抄録

We studied Cu/low-k integration to test the time-dependent dielectric breakdown (TDDB) reliability of Cu interconnects. We described the TDDB lifetime dependence on SiOC damage caused by sputtering and chemical-mechanical polishing (CMP) processes. The TDDB lifetime of the structure without a cap-SiO layer was three orders of magnitude shorter than that of the structure with the cap layer. However, the film properties of cap-SiO films thinner than 30 nm have a leakage path that allows TDDB degradation to occur easily. We also confirmed that narrowing of intermediate wiring levels with metal-to-metal spacing approaching 100nm degrades TDDB performance. Moreover, we showed the possibility that chemical attack and mechanical destruction during the polishing cause degradation of TDDB. Optimizing CMP conditions and eliminating the CMP-surface leakage path likely improve line-to-line insulating reliability, such as leakage current and TDDB, because these reliabilities are dominated by the extrinsic failure mode.

本文言語英語
ページ(範囲)4469-4474
ページ数6
ジャーナルJapanese Journal of Applied Physics
47
6 PART 1
DOI
出版ステータス出版済み - 6 13 2008

All Science Journal Classification (ASJC) codes

  • Engineering(all)
  • Physics and Astronomy(all)

フィンガープリント 「Study on factors in time-dependent dielectric breakdown degradation of Cu/low-k integration related to Cu chemical-mechanical polishing」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル