Study on the nature of the electrochemically synthesized hard Fe-15.4 mass% Ni-0.70 mass% C alloy film

A. S.M.A. Haseeb, Y. Hayashi, M. Masuda, M. Arita

研究成果: ジャーナルへの寄稿記事

抜粋

Electrochemical synthesis of hard Fe-15.4 mass% Ni-0.70 mass% C alloy film with a hardness 750 HV was carried out from sulfate-based bath containing a small amount of citric acid and L-ascorbic acid. The nature of the alloy was investigated by different characterization techniques including x-ray diffraction, x-ray photoelectron spectroscopy, scanning electron microscopy, transmission electron microscopy, Mössbauer spectroscopy, differential scanning calorimetry, and magnetic measurements. The decomposition behavior of the alloy was also studied and compared with that of thermally prepared martensite. It was found that the electrochemically deposited Fe-Ni-C alloy exists in a state that is ahead of the freshly quenched state of martensite. It is suggested that the state of the electrochemically deposited Fe-15.4 mass% Ni-0.70 mass% C alloy corresponds to the state of thermal martensite, which had been heated to the preprecipitation stage of tempering.

元の言語英語
ページ(範囲)840-847
ページ数8
ジャーナルJournal of Materials Research
18
発行部数4
DOI
出版物ステータス出版済み - 4 2003

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント Study on the nature of the electrochemically synthesized hard Fe-15.4 mass% Ni-0.70 mass% C alloy film' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用