Study on tritium release behavior from Li2ZrO3

T. Kanazawa, M. Nishikawa, H. Yamasaki, Kazunari Katayama, H. Kashimura, T. Hanada, Satoshi Fukada

研究成果: Contribution to journalArticle査読

5 被引用数 (Scopus)

抄録

The present authors have developed the tritium release model to represent the tritium release behavior from solid breeder materials (Li 2ZrO3, Li2TiO3, Li 4SiO4, LiAlO2 and Li2O). It has been found that water is released from solid breeder materials into the purge gas due to desorption of physically and chemically adsorbed water and water generation reaction and that this water affects the tritium release behavior. In this study, the amount of adsorbed water and its desorption rate for Li 2ZrO3 were quantified. It was found in this experiment that Li2ZrO3has the largest adsorption amount among the solid breeder candidates. It was also observed that Li2ZrO 3 has the largest water generation capacity among the solid breeder candidates. A unique reaction at around 550°C which made up approximately 80% of the capacity of water generation was also observed. It is considered that the phase change of ZrO2 at around 550°C supplies oxygen to promote water generation reaction. Tritium release behavior from Li 2ZrO3 blanket was estimated using the properties obtained in this study under the operational condition of ITER or a commercial reactor.

本文言語英語
ページ(範囲)1167-1170
ページ数4
ジャーナルFusion Science and Technology
60
3
DOI
出版ステータス出版済み - 1 1 2011

All Science Journal Classification (ASJC) codes

  • 土木構造工学
  • 核物理学および高エネルギー物理学
  • 原子力エネルギーおよび原子力工学
  • 材料科学(全般)
  • 機械工学

フィンガープリント

「Study on tritium release behavior from Li<sub>2</sub>ZrO<sub>3</sub>」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル