Superplasticity of liquid-phase-sintered β-SiC with Al2O3-Y2O3-AlN additions in an N2 atmosphere

Takayuki Nagano, Kenji Kaneko, Guo Dong Zhan, Mamoru Mitomo

研究成果: ジャーナルへの寄稿学術誌査読

26 被引用数 (Scopus)

抄録

Compression and tension tests were performed on liquid-phase-sintered β-SiC fabricated by hot-pressing, using ultrafine powders, at 1973-2048 K in an N2 atmosphere. Amorphous phases were observed at the grain boundaries and at multigrain junctions in the as-sintered material. Strain hardening was observed under all experimental conditions. Stress exponents in the compression test were 1.7-2.1 in the temperature range 1973-2023 K. A maximum tensile elongation of 170% was achieved at the initial strain rate of 2×10-5 s-1 at 2048 K.

本文言語英語
ページ(範囲)2497-2502
ページ数6
ジャーナルJournal of the American Ceramic Society
83
10
DOI
出版ステータス出版済み - 2000
外部発表はい

!!!All Science Journal Classification (ASJC) codes

  • セラミックおよび複合材料
  • 材料化学

フィンガープリント

「Superplasticity of liquid-phase-sintered β-SiC with Al2O3-Y2O3-AlN additions in an N2 atmosphere」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル