Synthesis and Aggregation Behavior of Poly(arylene alkenylene)s and Poly(arylene alkylene)s Having Dialkoxyphenylene and Aromatic Diimide Groups

Li Yi Tan, Yoshitaka Tsuchido, Kohtaro Osakada, Zhengguo Cai, Yoshiaki Takahashi, Daisuke Takeuchi

研究成果: Contribution to journalArticle

2 引用 (Scopus)

抜粋

Polycondensation reactions of 2,5-dialkoxy-1,4-diiodobenzene with N,N′-ω-dialkenylpyromellitic diimide and N,N′- ω-dialkenyl naphthalenetetracarboxylic diimide in the presence of a Pd(OAc) 2 -NaOAc catalyst produce six polymers containing the two aromatic groups connected alternatingly by alkenylene spacers. 1 H NMR spectrum of a polymer prepared from 2,5-bis(dodecyloxy)-1,4-diiodobenzene and N,N′-(10-undecenyl)pyromellitic diimide (poly(1a-IA)) indicates that the polymerization involves 2,1- and 1,2-insertion of a vinyl group into the Pd-Ar bond in 70:30 selectivity. Matrix-assisted laser deportion/ionization time-of-flight mass spectrometry (MALDI-TOF-MS) spectra of poly(1a-IA) and a polymer from 2,5-bis(dodecyloxy)-1,4-diiodobenzene with N,N′-dialkenyl naphthalenetetracarboxylic diimide (poly(1a-IIA)) contained a series of polymer fragments with M n up to 4500. Measurement of electrospray ionization MS (ESI-MS) of the polymers revealed formation of cyclic molecules for 1:1 and 2:2 oligomers. Hydrogenations of poly(1a-IA) by using [Ir(cod)(py)(PCy 3 )] + PF 6 - (cod = 1,5-cycloctadiene; PCy 3 = tricyclohexylphosphine) catalyst and of poly(1a-IIA) by a mixture of p-toluenesulfonyl hydrazide (TSH) and tripropylamine (TPA) produce the poly(arylene alkylene)s with saturated spacers in 93% degree of hydrogenation. The absorption spectrum of poly(1a-IA) in CHCl 3 shows an absorption edge at 410 nm, which is at a longer wavelength than that of a mixture of the monomers (370 nm). Light-scattering measurement of the solution (1.00 mmol L -1 ) indicates the presence of aggregates with a hydrodynamic radius of 48 nm. The polymers exhibit weak elasticity at room temperature, as determined by dynamic viscoelasticity analysis (DMA), and it becomes negligible on heating to 75-80 °C (polymer with pyromellitic diimide groups) and 110-122 °C (polymer with naphthalenetetracarboxylic diimide groups). The above properties of the polymers are attributed to attractive interaction between the electron-rich alkoxyphenylene and the electron-deficient aromatic diimide groups both in solution and in the solid state.

元の言語英語
ページ(範囲)1642-1652
ページ数11
ジャーナルMacromolecules
52
発行部数4
DOI
出版物ステータス出版済み - 2 26 2019

All Science Journal Classification (ASJC) codes

  • Organic Chemistry
  • Polymers and Plastics
  • Inorganic Chemistry
  • Materials Chemistry

フィンガープリント Synthesis and Aggregation Behavior of Poly(arylene alkenylene)s and Poly(arylene alkylene)s Having Dialkoxyphenylene and Aromatic Diimide Groups' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用