Synthesis and Characterization of Bioactive Quaternary Silicate Gel-glasses

T. T. Swe, H. Mohamad, K. A. Shariff, A. F.M. Noor, K. Ishikawa, A. A. Thant

研究成果: ジャーナルへの寄稿Conference article

2 引用 (Scopus)

抜粋

Bioactive glasses and glass-ceramics were applied in bone fix applications, dental applications as well as in tissue engineering. In the current study, a new quaternary silicate bioglass S50P4 (50%SiO2-24.5%Na2O-21.5%CaO-4%P2O5) with different aging time (3, 5 and 7 days) was prepared by sol-gel method. These synthesized glasses were analyzed using X-ray powder diffraction (XRD), Scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FTIR). Whereas the bioactivity of the optimized samples were observed through in-vitro test using Hank's Balanced Salt Solution (HBSS) at different soaking time (7 and 14 days). XRD results indicate that the crystalline patterns in gel-derived glass aged for 3 days exhibit stronger peaks compare to samples aged for 5 and 7 days. This could be attributed to the difference of water content inside the gels. Moreover, the peak at 2θ∼33° became sharper and more intense for longer soaking times corresponds to the apatite structure. Besides, in-vitro test shows, the formation of hydroxyl carbonated apatite layer (HCA) with finer grains.

元の言語英語
記事番号012070
ジャーナルJournal of Physics: Conference Series
1082
発行部数1
DOI
出版物ステータス出版済み - 10 10 2018
イベントRegional Conference on Materials and ASEAN Microscopy Conference 2017, RCM and AMC 2017 - Penang, マレーシア
継続期間: 12 12 201712 13 2017

All Science Journal Classification (ASJC) codes

  • Physics and Astronomy(all)

フィンガープリント Synthesis and Characterization of Bioactive Quaternary Silicate Gel-glasses' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用