Synthesis of crystalline SiC nanofiber through the pyrolysis of polycarbomethylsilane coated platelet carbon nanofiber

W. M. Qiao, S. Y. Lim, S. H. Yoon, I. Mochida, L. C. Ling, J. H. Yang

研究成果: Contribution to journalArticle査読

9 被引用数 (Scopus)

抄録

SiC nanofiber with high crystallinity was synthesized through the pyrolysis of polycarbomethylsilane (PS) coated platelet carbon nanofiber (PCNF) over 700 °C and burning PCNF under the oxidative atmosphere. The as-prepared β-SiC nanofiber exhibited a diameter less than 100 nm and a medium surface area of 50 m 2 /g. The crystallinity of silicon carbide (SiC) nanofiber increases with increasing heat-treatment temperature, showing the formation of high crystalline SiC nanofiber at 1400 °C. PCNF can be used as a unique template to govern the shape, crystallinity and morphology of SiC.

本文言語英語
ページ(範囲)4467-4471
ページ数5
ジャーナルApplied Surface Science
253
10
DOI
出版ステータス出版済み - 3 15 2007

All Science Journal Classification (ASJC) codes

  • 化学 (全般)
  • 凝縮系物理学
  • 物理学および天文学(全般)
  • 表面および界面
  • 表面、皮膜および薄膜

フィンガープリント

「Synthesis of crystalline SiC nanofiber through the pyrolysis of polycarbomethylsilane coated platelet carbon nanofiber」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル