Synthesis of highly transparent lithium ferrite nanoparticle/polymer hybrid self-standing films exhibiting faraday rotation in the visible region

Koichiro Hayashi, Rintaro Fujikawa, Wataru Sakamoto, Mitsuteru Inoue, Toshinobu Yogo

研究成果: Contribution to journalArticle査読

24 被引用数 (Scopus)

抄録

A lithium ferrite nanoparticle/ethyl(hydroxyethyl)cellulose (EHEC) hybrid was synthesized via in situ hydrolysis of prepolymerized iron(III) 3-allylacetylacetonate (IAA) and lithium acrylate (LA) in the presence of EHEC below 100 °C. The hybrid film was flexible and self-standing and showed high transmittance in the visible region. The crystallite size of lithium ferrite in the hybrid increased from 2.7 to 3.8 nm with decreasing amounts of EHEC. Nanosized lithium ferrite particle/EHEC hybrid showed a BH curve with no remanence at room temperature. The hybrid was superparamagnetic with a blocking temperature of 13 K. The absorption edge of the hybrid film was blue-shifted compared with bulk lithium ferrite. The blue-shift increased with decreasing crystallite size, which was controlled by the amount of EHEC. The self-standing film exhibited a Faraday rotation depending upon the magnetic field. The curve for the specific Faraday rotation (F) versus magnetic field corresponded to that for magnetization versus magnetic field. The figure of merit of the hybrid film was about 3.5 at 700 nm, which was higher compared with those of reported ferrite composite at shorter wavelengths, due to its high transparency.

本文言語英語
ページ(範囲)14255-14261
ページ数7
ジャーナルJournal of Physical Chemistry C
112
37
DOI
出版ステータス出版済み - 9 18 2008
外部発表はい

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Energy(all)
  • Physical and Theoretical Chemistry
  • Surfaces, Coatings and Films

フィンガープリント 「Synthesis of highly transparent lithium ferrite nanoparticle/polymer hybrid self-standing films exhibiting faraday rotation in the visible region」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル